Synthesis and Characterization of Graft Copolymers Containing Poly(P-Phenylene) Main Chains and Mesogen-Jacketed Liquid-Crystalline Polystyrene Side Chains

Li-Mei Sun,Xing-He Fan,Xiaci-Fang Chen,Xiang-Feng Liu,Qi-Feng Zhou

DOI: https://doi.org/10.1002/pola.22011

2007-01-01

Abstract:A series of novel comblike mesogen-jacketed liquid-crystalline graft copolymers, poly(p-phenylene)-g-polyl2,5-bis[(4-methoxyphenyl)oxycarbonyllstyrene) (PPP-gPMPCS) copolymers, have been designed and successfully synthesized by a Yamamoto coupling reaction and subsequent atom transfer radical polymerization (ATRP). H-1 NMR spectroscopy, ultraviolet-visible spectra, and gel permeation chromatography (GPC) have been used to confirm the molecular structure of the macroinitiator and the copolymers. A study of the polymerization kinetics of ATRP has shown that the molecular weight of the copolymer increases linearly with the conversion of the monomer, whereas the polydispersity remains narrow (<= 1.28), indicating that the ATRP of 2,5bis[(4-methoxyphenyl)oxycarbonyllstyrene is well controlled. Thermogravimetric analysis and differential scanning calorimetry (DSC) measurements have indicated that the PPP-g-PMPCS copolymers have better thermal stabilities than the macroinitiator, and their thermal stabilities increase with increasing molecular weight. The liquid-crystalline behavior has been examined with polarized optical microscopy, DSC, one-dimensional wide-angle X-ray diffraction (1D WAXD), and two-dimensional wide-angle X-ray diffraction (21) WAXD). The results show that all the comblike copolymers exhibit obvious liquid-crystalline behaviors, even though the GPC molecular weight of the segments of poly{2,5-bis[(4-methoxyphenyl)oxycarbonyllstyrenel} (PMPCS) have been determined to be far less than the critical value of linear PMPCS. Moreover, 11) WAXD measurements show that the temperature at which the comblike mesogen-jacketed liquidcrystalline copolymers can transform into a liquid-crystalline phase is low; about 20 degrees C in comparison with the linear ones. 21) WAXD analysis has revealed that these comblike copolymers should be assigned to a hexatic columnar nematic ((DHN)-D-Phi) phase. (C) 2007 Wiley Periodicals, Inc.