Design and Synthesis of a Series of Novel Mesogen-Jacketed Liquid Crystal Polymers

Hui l. Tu,Zhenning Yu,Xinhua Wan,Xiaofang Chen,Qifeng Zhou

2000-01-01

Abstract:This paper describes the synthesis and free radical polymerization of 2,5-bis(4'-alkyloxyphenyl) styrene(M-n) for mesogen-jacketed liquid crystal polymers(MJLCPs), where p-terphenyl subsituted by alkoxy groups at both ends was used as mesogenic unit. Because of the absence of the polar linkage groups, such as -COO- or -CONH- as employed in the previous reported MJLCPs, M-n is believed to be polymerized easily by both free radical polymerization and ionic polymerization. The chemical structure of M-n was proved by H-1 NMR, mass spectrometry and elementary analysis. Their phase transition and liquid crystallinity were characterized by DSC and POM, Although M-1, M-2, M-3 and M-4 exhibited monotropic nematic mesophase, M-5 displayed enantiotropic nematic mesophase presumably because of its decreased melting transition temperature, All monomers were easily polymerized to moderately high molecular weight polymers. At elevated temperature above T-g, poly[2,5-bis(4'-alkoxyphenyl) styrene] showed a very stable mesophase, The formed birefrigence did not disappear until thermal decomposition started. Compared to other MJLCPs, the polymers reported here have much higher thermal stability.