Synthesis and Characterization of N-phenyl Maleimide Modified Novolac Resin

ZHOU Dapeng,FAN Hong,BU Zhiyang,LI Bogeng

DOI: https://doi.org/10.3321/j.issn:0438-1157.2005.10.033

2005-01-01

Abstract:N-phenyl maleimide modified novolac resin was synthe sized by condensation polymerization of a mixture of N-phenyl maleimide and formaldehyde by slowly feeding phenol in the presence of an acid catalyst. The polymerization conditions were optimized to obtain the high reaction conversion of PMI and proper viscosity of PPMF. It was found that reaction competition an d conversion ratio for PMI were enhanced with increasing feeding time of phenol . As the reaction reflux time was increased, the conversion of PMI and the visc osity of PPMF were increased. At a higher reaction temperature or more amount o f PMI, the conversion of PMI was decreased. The resins were characterized by FT IR, 13C NMR and thermal analysis. It was found that the N-phenyl male imide groups were combined in the chains of novolacs and the N-phenyl malei mide content of PPMF could reach around 33%. DSC curve revealed two curing peak s,of which one at around 150℃ was attributed to the condensation reaction of me thylol groups formed in minor quantities on the phenyl rings,and the other at ar ound 250℃ was attributed to the addition curing reaction of the maleimide group s. TGA analysis showed that the cured PPMF had better thermal properties.