Abstract:A kind of modified bismaleimide resin, with good processability, heat resistance, and impact strength was developed, using 4,4 ′ -dipropargyloxydiphenyl ether (DPEDPE), N-(4-propargyloxyphenyl)maleimide (4-PPM), and 3-ethynylphenyl maleimide (3-EPM) as modifiers. The DPEDPE, 4-PPM, and 3-EPM were synthesized and characterized by Fourier transform infrared spectroscopy (FTIR) and 1 H-nuclear magnetic resonance ( 1 H NMR), and used to modify the N,N ′ -(4,4 ′ -diphenylmethane)bismaleimide (BDM)/2,2 ′ -diallyl bisphenol A (DABPA) resin system (BD) to obtain the different blend resin systems of DPEDPE-modified BD (BDD), 4-PPM-modified BD (BDP), and 3-EPM-modified BD (BDE). The curing temperature of BD resin increases with increase of the alkynyl-terminated modifier content. The processability of BD resin was improved with addition of the propargyloxy-terminated compounds. The temperature of 5% weight loss, residual yield at 800°C and glass transition temperature of the cured BD resin increase with increase of the alkynyl-terminated modifier content and can reach 443°C, 46.7% and higher than 380°C. The tensile strength of the cured BD resin decreases with increase of alkynyl-terminated modifier content. The impact strength of the cured BD resin increases with increase of the propargyloxy-terminated compound content and can increase by 65%. The tensile strength, elastic modulus, and impact strength of the cured BD resin blended with DPEDPE can be 73.7 MPa, 4.1 GPa, and 19.6 kJ m −2 , respectively. Moreover, the cured BD resin blended with DPEDPE has good water absorption resistance.

Preparation and Characterization of Multifunctional Maleimide Macromonomers and Their Cured Resins

Curing Behavior of the Bismaleimide Containing Ether Linkage and Naphthalene

Cure of Neat Resins and Properties of Composites for Interpenetrating Polymer Networks from the Novel Bismaleimide and Cyanate Containing Naphthalene

Study on Curing Kinetics and Thermal Properties of Bismaleimide Resin Containing Ether Linkage

Synthesis and Characterization of N-phenyl Maleimide Modified Novolac Resin

Preparation and Characterization of Bismaleimide-Diamine Prepolymers and Their Thermal-Curing Behavior

Synthesis and Cure of Liquid Crystalline Diallyl Modifiers for Bismaleimide Resin

Thermal properties of an epoxy cresol-formaldehyde novolac/diaminodiphenyl sulfone system modified by bismaleimide containing tetramethylbiphenyl and aromatic ether structures

Preparation And Characterization Of Novel Bismaleimide Resins Modified With Diallyl Bisphenol A

Novel Thermosetting Resins Based on 4-(N-maleimidophenyl)glycidylether I. Preparation and Characterization of Monomer and Cured Resins

Preparation And Properties Of Epoxy/Maleimide Compounds And Their Cured Resins

Novel Thermosetting Resins Based on 4-(N-maleimidophenyl)glycidylether: II. Bismaleimides and Polybismaleimides

Highly cross-linked thermosetting resin of maleimidobenzoxazine functionalized with benzocyclobutene

Bismaleimide-diamine copolymers containing phthalide cardo structure and their modified BMI resins

Synthesis, preparation and properties of novel high-performance allyl–maleimide resins

Thermosetting Resins Based on A Self-Crosslinkable Monomer/Polymer Possessing Meldrum'S Acid Groups

Meldrum's Acid-Functionalized Bismaleimide, Polyaspartimide and Their Thermally Crosslinked Resins: Synthesis and Properties

Synthesis and characterization of novel chain-extended bismaleimides containing fluorenyl cardo structure

Characterization and properties of high-temperature resistant structure adhesive based on novel toughened bismaleimide resins

Preparation and properties of bismaleimide resin blended with alkynyl-terminated modifiers

Selective reactivity of aromatic amines toward 5-maleimidoisophthalic acid for preparation of polyamides bearing N-phenylmaleimide moieties