Facile and low-cost production of TiO2 nanoparticles using high-energy milling for dye degradation

Athanasia Amanda Septevani,Yenni Apriliany Devy,Deni Shidqi Khaerudini,Melati Septiyanti,Yulianti Sampora

DOI: https://doi.org/10.1063/5.0060035

2021-01-01

Abstract:The production of TiO2 nanoparticle via scalable and facile method is of importance to fulfil the increasing demand of TiO2 as semiconductor and photocatalytic agent. Commercial technical grade of TiO2 powder was high-energy ball milled in a various rotational speed by using Planetary Ball Mill PM 200. The effect of milling speed on the particle size, morphology, and crystallite phase of the obtained TiO2 powders were evaluated. The milling process at 400 rpm for 4 hours showed significant reduction of the particle size of TiO2 from 1595.4 ± 73.4 nm to be 358.9 ± 41.0 nm, which were comparable to the size of commercial nano powdered TiO2. The X-Ray Diffraction analysis showed the phase transformation of TiO2 from rutile to anatase, which could benefit for improving photocatalytic dye degradation. It was observed that the photocatalytic activities of the milled TiO2 was comparable to the commercially available nano TiO2 towards methyl orange and Rhodamine B in terms of efficiency of dye removal and final physical color change after the period of treatments. These results indicate that the high-energy milling offers the alternative and promising method for preparing low-cost of TiO2 nanoparticles for dye degradation.