Ce3+ doped Lu3Al5O12 ceramics prepared by spark plasma sintering technology using micrometre powders: Microstructure, luminescence, and scintillation properties
Yun Shi,Oleg Shichalin,Yifei Xiong,Denis Kosyanov,Tong Wu,Qian Zhang,Ling Wang,Zhenzhen Zhou,Hui Wang,Jinghong Fang,Huan He,Jinqi Ni,Chaoyue Wang,Qian Liu,Jianding Yu,Sheng Cui,Haibo Wang,Anton Belov,Eugeniy Papynov
DOI: https://doi.org/10.1016/j.jeurceramsoc.2022.07.014
IF: 5.7
2022-11-01
Journal of the European Ceramic Society
Abstract:Ce3+ doped Lu3Al5O12 (Ce:LuAG) ceramics were fabricated by the solid-state reaction method through spark plasma sintering (SPS) from 1350 °C to 1700 °C for 5 min at a pressure of 50 MPa using micro powders. The average grain size of the SPSed ceramics gradually grew from 0.42 μm (1400 °C) to 1.55 μm (1700 °C), which is nearly one order of magnitude lower than that of vacuum sintered (VSed) Ce:LuAG ceramics (~24.6 μm). Characteristic Ce3+ emission peaking at around 510 nm appeared and 92% photoluminescence intensity of room temperature can be reserved at 200 °C revealing excellent thermal stability. The maximum radioluminescence intensity reached around 3 times of VSed Ce:LuAG ceramics and 7.8 times of BGO crystals. The maximum scintillation light yield under γ-ray (137Cs) excitation reached 9634 pho/MeV @ 2 μs. It is concluded that SPS technology is a feasible way to develop Ce:LuAG ceramics and further optical enhancement can be expected.
materials science, ceramics