Abstract:In this work, the structural and mechanical properties of ternary Mo-Al-N alloys are investigated by combining thin film growth experiments and density functional theory (DFT) calculations. Mo1−xAlxNy thin films (∼300 nm thick), with various Al fractions ranging from x = 0 to 0.5 and nitrogen-to-metal (Al + Mo) ratio ranging from y = 0.78 to 1.38, were deposited by direct-current reactive magnetron cosputtering technique from elemental Mo and Al targets under Ar + N2 plasma discharges. The Al content was varied by changing the respective Mo and Al target powers, at a fixed N2 (20 SCCM) and Ar (25 SCCM) flow rate, and using two different substrate temperatures Ts = 350 and 500 °C. The elemental composition, mass density, crystal structure, residual stress state, and intrinsic (growth) stress were examined by wavelength dispersive x-ray spectroscopy, x-ray reflectivity, x-ray diffraction, including pole figure and <math> si n 2 ψ</math> measurements, and real-time in situ wafer curvature. Nanoindentation tests were carried out to determine film hardness H and elastic modulus EIT, while the shear elastic constant C44 was measured selectively by surface Brillouin light spectroscopy. All deposited Mo1−xAlxNy films have a cubic rock-salt crystal structure and exhibit a fiber-texture with a [001] preferred orientation. The incorporation of Al is accompanied by a rise in nitrogen content from 44 to 58 at. %, resulting in a significant increase (2%) in the lattice parameter when x increases from 0 to 0.27. This trend is opposite to what DFT calculations predict for cubic defect-free stoichiometric Mo1−xAlxN compounds and is attributed to variation in point defect concentration (nitrogen and metal vacancies) when Al substitutes for Mo. Increasing Ts from 350 to 500 °C has a minimal effect on the structural properties and phase composition of the ternary alloys but concurs to an appreciable reduction of the compressive stress from −5 to −4 GPa. A continuous increase and decrease in transverse sound velocity and mass density, respectively, lead to a moderate stiffening of the shear elastic constant from 130 to 144 GPa with increasing Al fraction up to x = 0.50, and a complex and nonmonotonous variation of H and EIT is observed. The maximum hardness of ∼33 GPa is found for the Mo0.81Al0.19N1.13 film, with nitrogen content close to the stoichiometric composition. The experimental findings are explained based on structural and elastic constant values computed from DFT for defect-free and metal- or nitrogen-deficient rock-salt MoAlN compounds.

Correlation between optical properties of MBE films of AlN and morphology of their surface

High-quality AlN growth: a detailed study on ammonia flow

The optical properties and applications of AlN thin films prepared by a helicon sputtering system

Epitaxial AlN film with improved quality on Si (111) substrates realized by boron pretreatment via MOCVD

Optical and Structural Investigation of AlN Grown on Sapphire with Reactive MBE Using RF Nitrogen or Ammonia

Nanorelief of the Surface of Thin Films of Al–Mn and Al–Ni Alloys upon Ion-Assisted Deposition on Glass

Structural, chemical and optical characterizations of nanocrystallized AlN:Er thin films prepared by r.f. magnetron sputtering

Comparative spectroscopic studies of MOCVD grown AlN films on Al2O3 and 6H–SiC

Optical band gap and associated band-tails in nanocrystalline AlN thin films grown by reactive IBSD at different substrate temperatures

Optical and Structural Properties of Aluminum Nitride Epi-Films at Room and High Temperature

Growth-microstructure-thermal property relations in AlN thin films

Optical properties and hardness of highly a-axis oriented AlN films

Effect of nitrogen flow ratio on the structure and optical properties of AlN film

Comparison of aluminum nitride thin films prepared by magnetron sputter epitaxy in nitrogen and ammonia atmosphere

Temperature Dependence of Stress and Optical Properties in AlN Films Grown by MOCVD

Influence of the Nucleation Layer Morphology on the Structural Property of AlN Films Grown on C-Plane Sapphire by MOCVD

Real-time in situ ellipsometric monitoring of aluminum nitride film growth via hollow-cathode plasma-assisted atomic layer deposition

Morphology Evolution, Growth Mechanism and Optical Properties of AlN Nanostructures

Surface chemistry in atomic layer deposition of AlN thin films from Al(CH3)3 and NH3 studied by mass spectrometry

Impact of Temperature and Substrate Type on the Optical and Structural Properties of AlN Epilayers: A Cross-Sectional Analysis Using Advanced Characterization Techniques

Structure, stress, and mechanical properties of Mo-Al-N thin films deposited by dc reactive magnetron cosputtering: Role of point defects