Effect of particle size and composition on local magnetic hyperthermia of chitosan-Mg1−xCoxFe2O4 nanohybrid
M. Aminul Islam,Ishtiaque M. Syed,M. Al Mamun,S. Manjura Hoque
DOI: https://doi.org/10.3389/fchem.2024.1347423
IF: 5.5
2024-03-08
Frontiers in Chemistry
Abstract:In this study, Mg 1 −x Co x Fe 2 O 4 (0 ≤ x ≤ 1 with ∆x = 0.1) or MCFO nanoparticles were synthesized using a chemical co-precipitation method and annealed at 200, 400, 600, and 800°C respectively to investigate the structural properties of the materials by X-ray diffractometer (XRD), transmission electron microscopy (TEM), and Fourier-transform infrared spectroscopy (FTIR). Controlled annealing increased particle size for each value of x. The aim was to investigate how specific loss power (SLP) and maximum temperature (T max ) during local magnetic hyperthermia were affected by structural alterations associated with particle size and composition. The lattice parameter, X-ray density, ionic radius, hopping length, bond length, cation-cation distance, and cation-anion distance increase with an increase in Co 2+ content. Raman and FTIR spectroscopy reveal changes in cation distribution with Co 2+ content and particle size. Magnetic properties measured by the physical property measurement system (PPMS) showed saturation magnetization (M s ), coercivity (H c ), remanent magnetization (M r /M s ), and anisotropy constant (K 1 ) of the Mg 1 −x Co x Fe 2 O 4 nanoparticles increase with Co 2+ content and particle size. When exposed to an rf magnetic field, the nanohybrids experienced an increase in both the SLP (specific loss power) and T max (maximum temperature) as the particle size initially increased. However, these values reached their peak at critical particle size and subsequently decreased. This occurs since a modest increase in anisotropy, resulting from the presence of Co 2+ and larger particle size, facilitates Néel and Brownian relaxation. However, for high anisotropy values and particle size, the Néel and Brownian relaxations are hindered, leading to the emergence of a critical size. The critical size increases as the Co 2+ content decreases, but it decreases as the Co 2+ content increases, a consequence of higher anisotropy with the increase in Co 2+ . Additionally, it is noteworthy that the maximum temperature (T max ) rises as the concentration of nanohybrids grows, but the specific loss power (SLP) decreases. An increased concentration of chitosan-MCFO nanohybrids inhibits both the Néel and Brownian relaxation processes, reducing specific loss power.
chemistry, multidisciplinary