Synthesis of the Magnetite Water-Based Nano-Magnetic Fluid and Their Inductive Heating Property in Alternating Current Magnetic Field

Ying Xu,Dong-lin Zhao,Ling-yun Zhao,Jin-tian Tang

2010-01-01

Abstract:The Fe3O4 nanoparticles modified by sodium oleate with a diameter of 10-25 nm were prepared by coprecipitation. The inductive heating property of nano Fe3O4 water-based magnetic fluid in an alternating current magnetic field was investigated. The potential of the nano Fe3O4 water-based magnetic fluid was evaluated for tumor thermotherapy. FT-IR spectrum shows the sodium oleate was absorbed on the magnetite surface via chemical adsorption. When the coprecipitation temperature were 80 degrees C, the inductive heating property of the nano Fe3O4 water-based magnetic fluids increased first and then decreased with the molar ratio of Fe2+ and Fe3+. As the molar ratio of Fe2+ and Fe3+ was more than 2:1, exposed in the alternating current magnetic field for 1 min, the temperatures of the Fe3O4 water-based nano-magnetic fluids were higher than 45 degrees C. When the molar ratio of Fe2+ and Fe3+ were 4:1, the inductive heating property of the nano Fe3O4 water-based magnetic fluids increased first and then decreased with the coprecipitation temperature. As the coprecipitation temperature was higher than 50 degrees C, exposed in the alternating current magnetic field for 1 min, the temperatures of the Fe3O4 water-based nano-magnetic fluids were higher than 45 degrees C. The nano Fe3O4 water-based magnetic fluids will be useful for tumor therrnotherapy.