Abstract:Aerogel has been widely known as a low-density and highly porous material and is closely connected with the complex processing methods, such as freeze–drying or supercritical drying. In this work, using the polymerization-induced aramid nanofiber (PANF) as a building block, we put forward a modified freezing–drying method for the high-efficiency preparation of all-<i>para</i>-aromatic-amide aerogels. In the preparation process, PANF hydrogel is first frozen at −18 °C and then dried at 20–150 °C for the formation of PANF aerogel. The PANF framework formed during the freezing process is crucial for the formation of the PANF aerogel. Moreover, the space-occupying effect of ice crystals is also helpful for the formation of the macroscopic pore structure in the aerogel. Aerogels with large size or well-controlled shape could be successfully obtained by this method. Through the variation of PANF concentration in the hydrogel and drying temperature, aerogels with different densities (20–185 mg/cm<sup>3</sup>) could be achieved, and the lowest density is reached at 150 °C, with the PANF concentration of 0.7%. The low-density PANF aerogels show high specific compressive strengths and low thermal conductivities, which are comparable to those resulting from the freeze–drying or supercritical drying method. Furthermore, the shrinkage phenomenon in the drying process could be skillfully utilized for the preparation of PANF aerogel-coated objects. The PANF aerogels could be applied as a thermal insulating material or shock absorption material in practical applications.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.1c01551?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.1c01551</a>.Figure S1–S16: statistics of the diameter of PANFs; repeated filtering-dispersing process and PANF hydrogels with different PANF concentration; different products obtained from different methods; macroscopic state of PANF hydrogel and thawed PANF hydrogel before and after magnetic stirring; PANF hydrogel and the corresponding PANF aerogel in the shape of mooncake; preparation process of PANF aerogel-coated quartz tube; SEM images of different PANF aerogels at a low (×50) and high (×50000) magnification; high-temperature (150 °C) drying experiment for unfrozen and frozen PANF hydrogels with PANF% = 0.7%; specific strength of different PANF aerogel samples (ε = 70%); specific strength comparison of PA-20 and PA-40 with the low-density ANF-based aerogels (ε = 30%); compressive stress–strain curves of PA-20 at different strains for 100 compression–decompression cycles; surface of PANF aerogel before and after heating by infrared ray bulb; temperature variations of water in the metal tubes (with or without PANF aerogel insulation layer) after heating by infrared ray bulb; profiles of PANF aerogel and PU foam in the hot stage heating test; TGA and DTA curves of PANF aerogel and PU foam in air atmosphere; Tables S1–S3: stress retention and height recovery rates of PA-20 after 100 compression–decompression cycles at different strains; thermal conductivities of PANF aerogels and the already reported aramid aerogels; specific strengths (ε = 70%) and thermal conductivities of different kinds of aerogels (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.1c01551/suppl_file/nn1c01551_si_001.pdf">PDF</a>)Movie S1: Drop test of the PANF aerogel-coated quartz tube (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.1c01551/suppl_file/nn1c01551_si_002.avi">AVI</a>)This article has not yet been cited by other publications.

Effect of cooling rate on the microstructure absorption capacity of oil-based materials of graphene aerogels prepared by freeze casting at ambient pressure

Effect of Flake Size on the Mechanical Properties of Graphene Aerogels Prepared by Freeze Casting

Electromagnetic properties of graphene aerogels made by freeze-casting

Preparation of Anisotropic Aerogels with Pristine Graphene by Heat Flow and Study of Their Effects on Heat Transfer in Paraffin

Fabrication of super-elastic graphene aerogels by ambient pressure drying and application to adsorption of oils

Freeze‐Casting Mold‐Based Scalable Synthesis of Directional Graphene Aerogels with Long‐Range Pore Alignment for Energy Applications

Pristine Graphene Aerogels by Room-Temperature Freeze Gelation.

Optimizing the micro/mesoporous structure of hierarchical graphene aerogel for CO 2 capture by controlling the oxygen functional groups of graphene oxide

The preparation of graphene foam by one-step reduction and air-drying for oil–water separation

Control of microstructure to prepare compressible graphene aerogel via ice template

Macroscopic-Scale Preparation of Aramid Nanofiber Aerogel by Modified Freezing–Drying Method

Controllable preparation and electromagnetic wave absorption performance of compressible graphene aerogels

Bioinspired Manufacturing of Aerogels with Precisely Manipulated Surface Microstructure through Controlled Local Temperature Gradients

Graphene oxide aerogel ‘ink’ at room temperature, and ordered structures by freeze casting

Facile preparation of graphene aerogel as a thermal insulation material

Retarding Ostwald Ripening to Directly Cast 3D Porous Graphene Oxide Bulks at Open Ambient Conditions.

Low-density, high-strength and large-scaled monolithic carbon aerogels fabricated via modified ambient pressure drying

Intrinsically Microstructured Graphene Aerogel Exhibiting Excellent Mechanical Performance and Super-High Adsorption Capacity

Graphene aerogels as efficient adsorbers of water pollutants and their effect of drying methods

Graphene-Based Nanofluids: Production Parameter Effects on Thermophysical Properties and Dispersion Stability

Preparation and properties of cellulosenanofiber (CNF) /polyvinyl alcohol (PVA) /graphene oxide (GO): Application of CO2 absorption capacity and molecular dynamics simulation