Abstract:Fly ash has been widely explored in alkali-activated concrete technology as a precursor; however, it suffers sudden brittle failure and requires heat activation for early-strength development. Previous studies have demonstrated that these shortcomings can be overcome by adding nanosilica and various types of fibers. However, they were mainly focused on improving the mechanical properties, but there is no clear understanding of the durability and microstructural changes. Therefore, this study systematically addresses the effects of nanosilica sol and hybrid fibers (steel and polypropylene fibers) on the workability, porosity, flexural/ compressive strength development, flexural toughness, crack resistance, and durability (subjected to sulfuric acid of pH = 1, 5% sodium sulfate, and 3.5% seawater attacks) of fly ash-based mortars cured at ambient environments. The results demonstrate that nanosilica and hybrid fibers have acceptable simultaneous effects on the properties of mortar. Although they both reduce fluidity, nanosilica improves the pore enlargement caused by fiber materials; thus, it greatly improves the mechanical properties of mortar. The flexural toughness of the mortar with nanosilica and hybrid fibers was approximately 200% higher than that of the pure-fly ash. Only approximately 58.25 mm2 microcracks were observed during the early crack detection, and the residual strength also improved under chemical solution attack. The microstructures were studied by field-emission scanning electron microscopy with energy-dispersive X-ray spectroscopy, X-ray diffraction/Rietveld method, and nanoscale 3D X-ray microscopy. The nanosilica enhanced the reactivity of the precursors and refined the pore structure of the mortar due to the changes in the crystalline and amorphous phases, and the hybrid fibers produced composites with good internal characteristics and strong fiber/matrix interfacial bonding.

Characterisation and properties of class C-fly ash based geopolymer foams: Effects of foaming agent content, aggregates, and surfactant

Sulfate Resistance of Class C/class F Fly Ash Geopolymers

Synthesis of metakaolin-based geopolymer foamed materials using municipal solid waste incineration fly ash as a foaming agent

Mechanical Properties And Microstructure Of Class C Fly Ash-Based Geopolymer Paste And Mortar

Microstructure, Compressive Strength and Sound Insulation Property of Fly Ash-Based Geopolymeric Foams with Silica Fume as Foaming Agent

Physico-chemical properties and durability of a fly-ash-based geopolymer

Effect of Triterpenoid Saponins as Foaming Agent on Mechanical Properties of Geopolymer Foam Concrete

Thermal Resistance Variations of Fly Ash Geopolymers: Foaming Responses

Chloride resistance of class C/class F fly ash-based geopolymer mortars with different strength grades

Experimental study on full-volume fly ash geopolymer mortars: Sintered fly ash versus sand as fine aggregates

Utilization of Calcium Carbide Residue as Solid Alkali for Preparing Fly Ash-Based Geopolymers: Dependence of Compressive Strength and Microstructure on Calcium Carbide Residue, Water Content and Curing Temperature

Physico-mechanical, thermal insulation and resistance characteristics of diatomite and attapulgite based geopolymer foam concrete: Effect of different curing regimes

Compressive Strength and Thermal Conductivity of Fly Ash Geopolymer Concrete Incorporated with Lightweight Aggregate, Expanded Clay Aggregate and Foaming Agent

Development of Low-Calcium Fly Ash-Based Geopolymer Mortar Using Nanosilica and Hybrid Fibers

Effect of Elevated Temperature on Mechanical Properties of High-Volume Fly Ash-Based Geopolymer Concrete, Mortar and Paste Cured at Room Temperature

Effect of Silica Moduli on the Thermal Degradation Mechanisms of Fly Ash–Based Geopolymer Mortars

Physical and mechanical properties and micro characteristics of fly ash-based geopolymer paste incorporated with waste Granulated Blast Furnace Slag (GBFS) and functionalized Multi-Walled Carbon Nanotubes (MWCNTs)

Properties of cellular lightweight rubber wood fly ash geopolymer mortar containing cement

Residual water and interfacial bonding effects on the mechanical performance of CNT/fly ash geopolymer binder

Strength and microstructure of class C fly ash based geopolymer activated with sodium silicate powder

Mechanical Properties and Coagulation Characteristics of Flue Gas Desulfurization Gypsum-Based Polymer Materials