Abstract:Every structure might be exposed to fire at some point in its lifecycle. The ability of geopolymer composites to withstand the effects of fire damage early before it is put out is of great importance. This study examined the effects of fire on geopolymer composite samples made with high-calcium fly ash and alkaline solution synthesised from waste banana peduncle and silica fume. A ratio of 0.30, 0.35, and 0.4 was used in the study for the alkaline solution to fly ash. Also used were ratios of 0.5, 0.75, and 1 for silica oxide (silica fume) to potassium hydroxide ratio. The strength loss, residual compressive strength, percentage strength loss, relative residual compressive strength, ultrasonic pulse velocity, and microstructural properties of the thirteen mortar mixes were measured after exposure to temperatures of 200, 400, 600, and 800 °C for 1 h, respectively. The results reveal that geopolymer samples exposed to elevated temperatures showed great dimensional stability with no visible surface cracks. There was a colour transition from dark grey to whitish brown for the green geopolymer mortar and brown to whitish brown for the control sample. As the temperature rose, weight loss became more pronounced, with 800 °C producing the most significant weight reduction. The optimum mixes had a residual compressive strength of 25.02 MPa after being exposed to 200 °C, 18.72 MPa after being exposed to 400 °C, 14.04 MPa after being exposed to 600 °C, and 7.41 MPa after being exposed to 800 °C. The control had a residual compressive strength of 8.45 MPa after being exposed to 200 °C, 6.67 MPa after being exposed to 400 °C, 3.16 MPa after being exposed to 600 °C, and 2.23 MPa after being exposed to 800 °C. The relative residual compressive strength decreases for green geopolymer mortar are most significant at 600 and 800 °C, with an average decrease of 0.47 and 0.30, respectively. The microstructure of the samples revealed various phase changes and new product formations as the temperature increased.

Effect of Silica Moduli on the Thermal Degradation Mechanisms of Fly Ash–Based Geopolymer Mortars

Effects of Activator Types on Degradation Mechanisms of Metakaolin Geopolymer Mortars Exposed to High Temperature

High temperature resistance of fly ash/GGBFS-based geopolymer mortar with load-induced damage

Effect of Elevated Temperature on Mechanical Properties of High-Volume Fly Ash-Based Geopolymer Concrete, Mortar and Paste Cured at Room Temperature

Synergistic Effect of Blended Precursors and Silica Fume on Strength and High Temperature Resistance of Geopolymer

Study on the high-temperature resistance of metakaolin-fly ash-based geopolymers

Microstructural Analysis of Low-Calcium Fly Ash-Based Geopolymer Concrete with Different Ratios of Activator and Binder Under High Temperatures

Short-term residual characteristics of ambient-cured green geopolymer mortar exposed to elevated temperatures

The Influence of Particle Size and Calcium Content on Performance Characteristics of Metakaolin- and Fly-Ash-Based Geopolymer Gels

Studies on the performance of alkali-activated aluminosilicate geopolymer mortar against exposure to acid, sulfate, and elevated temperature

Thermal Properties of Geopolymer Based on Fayalite Waste from Copper Production and Metakaolin

XRD and TG-DTA Study of New Alkali Activated Materials Based on Fly Ash with Sand and Glass Powder

Thermal behavior of coal fly ash geopolymers: structural analysis supported by molecular dynamics and machine learning methods

Reaction Kinetics of Red Mud-Fly Ash Based Geopolymers: Effects of Curing Temperature on Chemical Bonding, Porosity, and Mechanical Strength

The Effect of Different Curing Temperatures on the Properties of Geopolymer Reinforced with Micro Steel Fibers

Effect of addition diatomite powder on mechanical strength, elevated temperature resistance and microstructural properties of industrial waste fly ash-based geopolymer

Thermal Resistance Variations of Fly Ash Geopolymers: Foaming Responses

Efflorescence of fly ash-based geopolymer mortars under quasinatural conditions: The relationship between curing temperature, ion transport, and compressive strength

Influence of Activators on Mechanical Properties of Modified Fly Ash Based Geopolymer Mortars

Characterisation and properties of class C-fly ash based geopolymer foams: Effects of foaming agent content, aggregates, and surfactant

Effect of Fine Aggregate Particle Characteristics on Mechanical Properties of Fly Ash-Based Geopolymer Mortar