Abstract:Laser metal deposition (LMD) is of the directed energy deposition (DED) process which is widely used for producing large-scale, dense, and functional parts in the field of additive manufacturing (AM). This research work investigates the microstructure and mechanical properties of PH 13–8 Mo martensitic stainless-steel parts produced via LMD. The workshop trials were conducted using an LMD system collaborated with a robotic arm to deposit single-track thin walls and horizontal blocks. The microstructural characteristics of the additively manufactured parts were analyzed using an optical microscope. The mechanical properties were evaluated through hardness measurements and uniaxial tensile tests. The influence of energy density and powder deposition density on the characteristic geometry of straight walls was also investigated. The microstructural analysis showed that the microstructure consisted of columnar dendrites that grew epitaxially from the substrate, with primary austenite cells containing intercellular ferrite and martensite laths that were roughly parallel with the retained austenite. When the energy density increased from 43 to 86 J/mm 2 (a doubling of energy density), there was an increase in secondary dendritic arm spacing (SDAS) by approximately 250% in the first layer and approximately 90% in the top layer. The difference in SDAS change between the first and top layers can be attributed to the difference in cooling rates experienced by each layer during the additive manufacturing process. Increasing powder deposition density from 0.5 to 1 g/min results in a decrease in porosity from 3% to less than 1% and an increase in strength from 800 to over 1000 MPa. The hardness of the deposits was found to range from 300 to 400 HV. This variation in hardness can be attributed to differences in microstructure resulting from changes in cooling rates at different heights.

Development of high intensity multibeam laser metal deposition system with blue diode lasers for additively manufacturing of copper rod

Development of blue diode laser for additive manufacturing

Pure copper rod formation by multibeam laser metal deposition method with blue diode lasers

Bead-on-plate welding of pure copper with a 1.5-kW high-power blue diode laser

Effect of input energy on densification for pure copper fabricated by SLM with blue diode laser

Development of an all-solid-state air-cooled high-power blue diode laser for metal processing

Pure copper layer formation on pure copper substrate using multi-beam laser cladding system with blue diode lasers

Experiment Study of Laser Thermal Enhanced Electrochemical Deposition

Melt pool behavior of pure copper-stainless steel multi-materials fabricated by the coaxial hybrid blue-infrared lasers additive manufacturing

Hybrid laser system with blue laser and near-infrared fiber laser for copper welding

Effect of blue diode laser intensity on welding of pure copper wire using blue-IR hybrid laser

Laser additive manufacturing of a 316L/CuSn10 multimaterial coaxial nozzle to alleviate spattering adhesion and burning effect in directed energy deposition

Metal 3d printing using high brightness blue laser systems

Wire Laser Metal Deposition Additive Manufacturing of Duplex Stainless Steel Components—Development of a Systematic Methodology

Study on laser welding of copper material by hybrid light source of blue diode laser and fiber laser

Enhanced electrical and mechanical properties of additively manufactured pure copper with green laser

Geometrical study of 5356 aluminium alloy by means of a concentric wire laser metal deposition

Stable conduction mode welding of conventional high-reflectivity metals with 2000 W blue laser

Additive and Photochemical Manufacturing of Copper

Molten pool structure and temperature flow behavior of green-laser powder bed fusion pure copper

Directed energy deposition of PH 13–8 Mo stainless steel: microstructure and mechanical property analysis