Abstract:Aluminum and its alloys find widespread applications across diverse industries such as the automotive, construction, and aeronautics industries. When these alloys come into contact with ambient air, an Al2O3 thin oxide layer is naturally formed, typically measuring 2 to 4 nm and exhibiting remarkable hardness and protective qualities, rendering the alloys corrosion-resistant in specific atmospheric and chemical environments. This study aimed to characterize the electrochemical behaviors of anodized AA2024 and AA7075 alloys within a complex three-component electrolyte composed of tartaric–phosphoric–sulfuric acid (TPSA) solutions. The anodized specimens were subsequently exposed to 3.5 wt.% NaCl solution at room temperature, and their electrochemical performances were meticulously evaluated using an electrochemical noise (EN) analysis in accordance with ASTM G-199, respectively. In the EN, three methods of data analysis were used: the time domain analysis (chaos analysis: application of Lyapunov exponent and dimension correlation), the frequency domain analysis (power spectral density, PSD), and the time–frequency domains analysis (Hilbert–Huang transform, HHT). Scanning electron microscopy (SEM) was used to observe the morphologies of the anodized surfaces. The results indicated that the AA2024-0, AA2024-1, and AA2024-2 alloys and the AA7075-2 and AA7075-3 samples exhibited mixed corrosion according to the Lyapunov constant, with a notable inclination towards localized corrosion when analyzed using the PSD and HHT methods. The surface was not homogenous, and the corrosion process was predominately localized in specific zones.

Electrochemical Noise Generation During Stress Corrosion Cracking of the High-Strength Aluminum AA 7075-T6 Alloy

Analysis of Electrochemical Noise Data of Stress Corrosion Cracking of High-Strength Carbon Steel in Acidified NaCl Solution

Electrochemical Noise Detection for SCC Behavior for 2024-T351 Aluminium Alloy in Acid NaCl Solution

Electrochemical noises of LC4, LY12 and pure Al in NaCl solution

Electrochemical noise features of pure aluminum during pitting corrosion in neutral NaCl solution

Electrochemical Noise Analysis Using Experimental Chaos Theory, Power Spectral Density and Hilbert–Huang Transform in Anodized Aluminum Alloys in Tartaric–Phosphoric–Sulfuric Acid Solutions

Electrochemical Noise Analysis of Local Pitting Corrosion Behavior of Pure Aluminum

Study of the Potential Electrochemical Noise During Corrosion Process of Aluminum Alloys 2024, 7075 and Pure Aluminum

ELECTROCHEMICAL NOISE OF AZ31 MAGNESIUM ALLOY IN NaCI SOLUTION

Electrochemical Noise Analysis of the Corrosion Behaviors of Al-Zn- in Based Alloy in NaCl Solution

Electrochemical Noise Characteristics in Corrosion Process of Az91d Magnesium Alloy in Neutral Chloride Solution

Features of Electrochemical Noise During Pitting Corrosion of 2024-T3 Aluminum Alloy in 3.0% Na2SO4 Solution

Electrochemical Noise Analysis of the Corrosion of AZ91D Magnesium Alloy in Alkaline Chloride Solution

Wavelets Analysis of Electrochemical Noise Generated During Corrosion Processes of Pure Al in NaCl Solution

ELECTROCHEMICAL FEATURES OF THE CORROSION OF AN ALUMINUM-LITHIUM ALLOY IN 3.0% NaCl SOLUTION

Anodic Dissolution-Based Mechanism for the Rapid Cracking, Preexposure Phenomenon Demonstrated by Aluminum-Lithium-Copper Alloys

Understanding Stress Corrosion Cracking Behavior of 7085-T7651 Aluminum Alloy in Polluted Atmosphere

Resistance to Stress Corrosion Cracking of New Al-Mg-Cu Alloy Containing Sc

ELECTROCHEMICAL NOISE ANALYSIS FOR CORROSION OF AZ91D MAGNESIUM ALLOY IN ALKALINE CHLORIDE MEDIUM

Nucleation of stress corrosion cracking in aluminum alloy 6061 in sodium chloride solution: Mechanical and microstructural aspects

Investigation of Stress Corrosion Cracking Susceptibility of 7A52 Aluminum Alloy under Different Applied Potentials