Abstract:Zirconium alloys have been used as primary materials for fuel cladding which protect the nuclear fuel from the outside in the nuclear power system. Zirconium alloys have very low absorption cross-section of thermal neutrons, high hardness, ductility, and corrosion resistance [1]. However, they had problems with nuclear reactor safety as they reacted violently with steam at high temperature, producing large amounts of hydrogen and heat, and having low mechanical strength at high temperature. Moreover, a massive hydrogen explosion by zirconium-steam interaction occurred at the Fukushima Daiichi nuclear power plant. The development of accident-tolerant fuel cladding has been widely studied since the Fukushima nuclear reactor accident [2]. Ideas and new concepts have been proposed for accident-tolerant fuel cladding to prevent hydrogen explosion by inhibiting reaction with steam in the accident environment. Therefore, the ATF research was actively carried out in the early development period to replace zirconium alloys using materials such as SiC, FeCrAl, etc., which have oxidation resistance better than zirconium [3,4]. However, the phenomenon of dissolution in cooling water under normal operating conditions was observed, and some materials had lower economic feasibility because the neutron absorption cross-section area was larger than zirconium. To overcome these problems, many researches are underway to take both stability and economy by coating the surface of zirconium cladding. By applying coating technology to zirconium cladding, it is easy to obtain corrosion resistance without a change in the base materials. Recently, Terrani et al. reported the oxidation resistance of Fe-based alloys for protecting zirconium alloys from the rapid oxidation in a high-temperature steam environment. Kim and co-workers also reported the corrosion behavior of Cr-coated zirconium alloy using a plasma spray and laser beam scanning [5]. In the present work, Cr anti-oxidation coating was fabricated on a commercial Zircaloy-4 cladding using cathodic arc ion plating (CAIP) because cathodic arc ion plated films tend be denser and have better adhesion characteristics than films produced using other method [6]. The Cr system was selected because of its good corrosion resistance. The microstructures of arc ion plated Cr coating were characterized. The oxidation behavior of the coating was analyzed. . 2. Experimental CAIP is well recognized method of producing protective coatings due to its high ionization efficiency and excellent film adhesion. It is a promising method for depositing oxidation-resistant coatings on nuclear fuel claddings. Pure Cr coating was deposited on the Zircaloy-4 using the CAIP with Cr target (99.59% purity). Figure. 1 shows the CAIP system which was designed to coat protective film onto the surface of a nuclear cladding. The substrates were cleaned ultrasonically in acetone and an ethanol solution, and the substrates were then mounted in a vacuum chamber. The chamber was evacuated to a pressure of 1 x 10 Torr, and heated simultaneously to 1473 K to remove the residual gas adsorbed on the chamber wall and substrates. Prior to the deposition, the substrates were sputter cleaned using Ar ions under -400V negative bias voltage for 5 min. Cr ion bombardment was applied to remove contaminants and ensure good adhesion of deposited coatings. The deposition of Cr was carried out in an Ar atmosphere with a pressure of 20mTorr. In order to study the effects of negative bias voltage, different negative bias voltages ranging from -25 to -100V were applied. After deposition, the coatings were polished to reduce the influence of the roughness, as well as for more precise measurements.

Post-LOCA ductility of Cr-coated cladding and its embrittlement limit

Post-quench ductility limits of coated ATF with various zirconium-based alloys and coating designs

Burst and oxidation behavior of Cr-coated Zirlo during simulated LOCA testing

Numerical Investigation of Ballooning and Burst for Chromium Coated Zircaloy Cladding

Fuel performance analysis of Cr-coated Zircaloy-4 cladding during a prototypical LOCA event using BISON

Effects of internal pressure and heating rate on the burst behaviors of Cr-coated cladding during simulated LOCA testing

In situ X-ray computed micro-tomography imaging of failure processes in Cr-coated Zircaloy nuclear fuel cladding materials

Chromium-coated cladding analysis under simulated LOCA burst conditions

Time in DNB experimental study on Cr coated zircaloy cladding

Performance Evaluation of Accident Tolerant Cr-coated Zr Alloy Cladding under Accident Conditions Based on a Refined Degradation Model

Corrosion Properties of Cr Coating Deposited on Nuclear Fuel Cladding

Microstructure Evolution and Failure Mechanism of Cr-coated Zry-4 in Air and Steam at 1200 °C

Effects of Pre-Crack Depth and Hydrogen Absorption on the Failure Strain of Zircaloy-4 Cladding Tubes Under Biaxial Strain Conditions

Expansion Deformation Mechanism and Cracking Behaviours of Chromium-Coated Zirconium Alloy Cladding at Room Temperature

Research on Compliance Between Large Break LOCA of HPR1000 and New LOCA Acceptance Criterion 10Cfr50.46c

Micro-mechanical evaluations of adhesion properties for Cr-coated accident tolerant fuel cladding

Behavior of high-velocity oxygen fuel sprayed chromium-coating on Zircaloy-4 fuel cladding under loss-of-coolant accident conditions

Expansion deformation mechanism and cracking behaviors of chromium-coated zirconium alloy cladding at room temperature

Elucidating changes in thermal creep strain rate of Cr-coated Zr-Nb alloy Accident Tolerant Fuel (ATF) cladding via experiment and mechanical analysis

Ductile tearing criteria and failure probability estimation of hydrided Zircaloy-4 cladding under axial loads

Degradation behavior of chromium-coated zirconium cladding under 1200 oC steam oxidation according to the coating microstructure