Abstract:Post Quench Ductility (PQD) of various Cr-coated cladding designs with respect to base cladding materials, Cr coating methods, and its thickness were investigated to explore Emergency Core Cooling System (ECCS) limits. Both inner wall and outer wall of coated (Cr and Cr/CrN) claddings were steam oxidized at ∼1204°C and then water quenched. The post-oxidized specimens were ring compressed to attain offset strains based on which ductility was assessed in compliance with the U.S. Nuclear Regulatory Commission (U.S. NRC)'s protocols. Weight gain-based Equivalent Cladding Reacted (ECR) limits of coated specimens (Cr and Cr/CrN) are consistently lower than those of the base cladding materials due to the early load drop under Ring Compression Test (RCT). Yet, time needed to reach the ECR limit is still increased for coated specimens because it effectively undergoes single side oxidation with protective coating. Cracks imitated from ZrCr 2 are primarily responsible for the early major load drop observed for tested coating thicknesses (8.9μm and 18.9μm), and hence reduced ECR limits compared to bare Zircaloy. The cracks from ZrCr 2 was promoted by an increased oxygen concentration of the interfacing Zr matrix owing to the diffusion of oxygen through the coating. The thicker coating reduces this oxygen level, thereby delaying the load drop from ZrCr 2 during RCT and increases the ECR limit. The maximum attainable ECR limit of coated ECR limits is affected by the base Zircaloy as it gives as the ECR ceiling from which ECR reduction for coated cladding occurs. For the tested base cladding materials (Opt. ZIRLO TM and HANA-6), ECR 19%, which is the limit for Cr-coated (8.9 μm) HANA-6, may serve as the lower envelope limit. Hence, ECR 19% (single-side ECR) can conservatively serve as the conservative, yet non-design specific, Cr-coated ECR limit for the most of the modern base Zircaloy materials (Opt. ZIRLO TM and HANA-6).

Expansion deformation mechanism and cracking behaviors of chromium-coated zirconium alloy cladding at room temperature

Expansion Deformation Mechanism and Cracking Behaviours of Chromium-Coated Zirconium Alloy Cladding at Room Temperature

Mechanical property and cracking mechanism of Cr-coated Zr alloy under tensile and compressive loading

Microstructure Evolution and Failure Mechanism of Cr-coated Zry-4 in Air and Steam at 1200 °C

Quantifying cracking and strain localisation in a cold spray chromium coating on a zirconium alloy substrate under tensile loading at room temperature

Structure and Oxidation Behavior of a Chromium Coating on Zr Alloy Cladding Tubes Deposited by High-Speed Laser Cladding

Oxidation Behavior of Cr-coated Zirconium Alloy Cladding in High-Temperature Steam above 1200 °C

Isothermal experiments on steam oxidation of magnetron-sputtered chromium-coated zirconium alloy cladding at 1200 °C

Systematic investigations on the microstructural evolution and degradation mechanism of Cr 3 Si-coated Zry-4 under DBA and BDBA conditions

High-Temperature Oxidation And Tensile Behaviors Of Cral Coating On Zirconium Alloy

Understanding Ion Transport Mechanisms of Chromium-Coated Zirconium Alloy Cladding in Steam Oxidation

Self-healing behavior of Cr-coated Zr alloy cladding in high temperature steam oxidation process

Post-quench ductility limits of coated ATF with various zirconium-based alloys and coating designs

Steam oxidation of Cr-coated zirconium alloy claddings at 1200 °C: Kinetics transition and failure mechanism of Cr coatings

Evolution of Cr/Cr2O3 interface in Cr-coated zirconium alloy in high temperature steam

The high-temperature oxidation and mechanical properties of the Cr/Zr and CrN/Zr coating

Insights into 1200 °C steam oxidation behavior of Cr coatings with different microstructure on Zircaloy-4 alloys for enhanced accident tolerant fuel cladding

In-situ study on the microstructure and cracking behavior of annealed Cr coated Zr-4 alloy

Model development for oxidation and degradation behavior of accident tolerant Cr coating on Zr alloy cladding under high temperature steam atmosphere

A comprehensive experiments and calculations on the Cr/Zr interface behaviour of Cr coated Zr cladding

In-situ study on the tensile property and fracture behavior of Cr coating for nuclear fuel cladding