Abstract:Titanium based IrO2+Ta2O5 oxide anodes with different compositions and pyrolysis temperatures were prepared by thermodecomposition method. By using X-ray diffraction (XRD), the structure and texture coefficient of the coatings. TC(hkl), of IrO2 rutile crystal have been tested. It showed that, the crystallization processes of IrO2 and Ta2O5 in IrO2+(100-x) Ta2O5 (x is in mol%) films affect and confine each other. In the mixed system, IrO2 rutile phase exists as a solid solution with Ta, and attains the maximum solubility when x=70 mol%, i.e. for the coating of 70% IrO2+Ta2O5. For the coatings of low iridium content or at low preparing temperature, (110) and (101) preferred orientations are dominant. However, preferred growth of IrO2 weakened with increasing either iridium content or temperature. Three typical surface morphologies were observed by using scanning electron microscopy (SEM). The crystallite size of the mixed oxide coatings are finest for the film of 70%IrO2+30%Ta2O5, and decreases with the pyrolysis temperature. As the results of the finest crystallite segregating on surface and the maximum solid solubility of Ir and Ta component in deposits, the coatings with the composition of 70%IrO2Y+Ta2O5 prepared at 450 °C present the maximum electrocatalytic activity for O2 evolution in 0.5 M H2SO4 solution. Up to 550°C, Ti base suffers to oxidation resulting in decreasing anode conductivity, therefore, coatings perform a low activity.

Influence of High-Temperature Water Vapor on Titanium Film Surface

Characterization of the Surface Oxygen-Diffusion Zone of the Thermally Oxidized Titanium

Bioactive treatment of titanium surface using a H2O2/HCl solution

Improvement of Bioactivity of H(2)O(2)/TaCl(5)-treated Titanium after Subsequent Heat Treatments.

Electrochromism of titanium oxide thin films

Surface Characterization of Thermally Oxidized Titanium Alloys

Effect of Annealing Temperature on Wettability of TiO2 Nanotube Array Films.

Temperature-dependent differences in wettability and photocatalysis of TiO 2 nanotube arrays thin films

Low-Temperature Deposition of Anatase Thin Films on Titanium Substrates and Their Abilities to Photodegrade Rhodamine B in Water

Crystallization Behaviors of TiO2 Films Derived from Thermal Oxidation of Evaporated and Sputtered Titanium Films

Natural Hydrophobicity and Reversible Wettability Conversion of Flat Anatase TiO₂ Thin Film.

Effect of the Substrate Temperature on the Crystallization of TiO2 Films Prepared by DC Reactive Magnetron Sputtering

In vitro bioactivity of anatase film obtained by direct deposition from aqueous titanium tetrafluoride solutions

Compositional and Structural Evolution of the Titanium Dioxide Formation by Thermal Oxidation

Corrosion Resistance and Ion Dissolution of Titanium Implant under Different Temperature Thermal Oxidation

Investigation of surface morphology, structure and electrocatalytic properties for O2 evolution of titanium based IrO2+Ta2O5 coatings

A Study of Titanium Oxide Film Electrodes Prepared by Direct Thermal Oxidation Ⅰ. Preparation, Structure and Electrochemical Properties

Oxidation Conditions of Ti and Photocatalysis of TiO2 Ceramic Films

Influence of Oxidation Process on Photocatalytic Activity of Photocatalyst Coatings by Mechanical Coating Technique

Structure and hydrophilicity of titanium dioxide film prepared by atmospheric pressure chemical vapor deposition

Effects of heat treatment on the microstructure and properties of TiO2 based film by plasma electrolytic oxidation