Abstract:In this study, the effect of different holding times at 1250 °C on acicular ferrite formation, the inclusion characteristics, and Mn depletion behavior at the inclusion-matrix interface in Ti-Mg oxide metallurgy steel was systematically investigated. The results suggested that the volume fraction of grain boundary products decreased with increased holding time from 60 s to 3600 s, with the volume fraction of acicular ferrite initially increasing and then decreasing. Regarding the inclusion characteristics, different holding times showed no obvious effect on the inclusion type, but they affected the size and area number density of the inclusions. The domain inclusions at different holding times all consisted of MgTi 2 O 4 +MnS, and these inclusions were found to be effective for the nucleation of acicular ferrite. The average diameter of the inclusions increased, and the area number density of the effective inclusions significantly decreased when the holding time was increased from 900 s to 1800 s and 3600 s. Mn-depleted zones (MDZs) with larger widths and higher Mn concentration gradients formed at the inclusion-matrix interfaces at holding times of 60 s and 900 s, and MDZ formation was weakened by the continuous diffusion of Mn when the holding time was increased to 1800 s and 3600 s. At a holding time of 900 s for the Ti-Mg oxide metallurgy steel, the volume fraction and relative nucleation potential of acicular ferrite reached their maximum values, and MDZ formation with the lowest Mn concentration (∼0.8 wt%) was observed around the MgTi 2 O 4 +MnS inclusions. Therefore, 900 s was the optimal holding time for acicular ferrite formation.

Precipitation behaviour of oxide in directionally solidified aerospace bearing steel

A Study of the Corrosion Resistance of M50NiL Bearing Steel by Ion Implantation

Elimination and Control of δ Ferrite in M50NiL Bearing Steel

Precipitation Behavior of Laves Phase in the Vicinity of Oxide Film of Ferritic Stainless Steel: Selective Oxidation-Induced Precipitation

Microstructure evolution and solidification behaviour of Nb–16Si–22Ti–2Cr–2Al–6Hf alloy processed by directional solidification

Revolution and Control of Fe-Al-(Mg, Ti)-O Oxide Inclusions in IF Steel during 260t BOF-RH-CC Process

Achieving Superior High-Temperature Strength and Oxidation Resistance of TiAl Nanocomposite through In Situ Semicoherent MAX Phase Precipitation

The investigation of precipitation behavior of titanium compounds for high titanium steel based on in situ observation

Precipitate Formations with Self-Adaptive Elemental Diffusion and Segregation in T92 Steel

On the Orientation Relationship Between Ti5Si3 Precipitates and B2 Phase in a Ti-47Al-2W-0.5Si Alloy

Revealing High-Temperature Oxidation and Tensile Behaviors along with Underlying Mechanisms of a Titanium Alloy with Precipitated Titanium Silicide

Effect of aluminum addition on microstructure, mechanical properties and high temperature tribological properties of nickel-rich NiTi alloy

High Temperature Oxidation Behavior of Directionally Solidified Fe(Al,Ta)/Fe2Ta(Al) Eutectic Composite

Microstructure and segregation behaviour of directionally solidified tungsten bearing 25Cr-35Ni-Nb heat-resistant stainless steels

Microstructural Evolution of Al-Si Alloy above Liquidus Temperature during Holding Temperature

Acicular ferrite formation and Mn depletion behavior around the inclusions in Ti-Mg oxide metallurgy steel with different holding times

Secondary Phase Precipitation in Fe-22Mn-9Al-0.6C Low-Density Steel during Continuous Cooling Process

Precipitation Behavior of Nb in Steel under Ultra Fast Cooling Conditions

Thermodynamics on compositional design of slag for the Ti content control in bearing steel

Microstructure evolution during oxidation of quinary Ti 3 (AlSiSn)C 2 at high temperatures and induced probable performance