Abstract:Based on micron atomized spherical Cu-18Sn-0.3Ti alloy powders, the Cu-18Sn-0.3Ti alloy with an elongation of 23.4%, an ultimate tensile strength of 507.2 MPa and a yield strength of 229.4 MPa was prepared using Direct Current assisted Hot Pressed sintering (DCHP) and conventional solution treatment. The microstructure evolution mechanism of alloy during DCHP, the strength-ductility synergy and fracture mechanisms of solution treated DCHP (ST-DCHP) samples were systematically investigated. The results show that, under the synergistic effect of Joule heat, electron wind force and external load of DCHP, dislocations were consecutively generated and consumed as the driving force of dynamic recrystallization, fine equiaxed grains and a large number of annealing twins were formed, the prior particle boundaries (PPBs) of alloy powders gradually disappeared and good sintering necks were formed, which played key roles in improving the strength of alloy. Simultaneously, the δ phase was segregated from grain boundaries to PPBs during DHCP. During the subsequent solution treatment, the phase transformation of δ phase occurred, the β, γ and ε phases which were conducive to the plastic deformation of alloy were generated inside δ phase, resulting in a change in the fracture mechanism inside powders and at sintering necks. The high fraction of high-angle grain boundaries (HAGBs) was considered as the main reason for inducing the formation of high-density deformation twins with different directions inside fine α grains, which greatly improved the ductility of alloy. The strengthening contributions of microstructure were also evaluated, and the calculated yield strength was well consistent with the experimental ones. The results provide the theoretical guidance for the preparation of Cu-Sn-Ti alloy with higher Sn content and lay a foundation for the preparation of Nb3Sn superconducting wires with higher critical current density.

Mechanical Properties and Microstructural Characterization of Cu-4.3 Pct Sn Fabricated by Selective Laser Melting

Processing Technologies and Properties of Cu-10Sn Formed by Selective Laser Melting Combined with Heat Treatment

Selective Laser Melting of Cu–10Sn–0.4P: Processing, Microstructure, Properties, and Brief Comparison with Additively Manufactured Cu–10Sn

Microstructure Twinning and Mechanical Properties of Laser Melted Cu-10Sn Alloy for High Strength and Plasticity

Microstructure and tensile properties of Sn-1Cu lead-free solder alloy produced by directional solidification

Microstructure evolution, strength-ductility synergy and fracture mechanisms of Cu-18Sn-0.3Ti alloy prepared using Direct Current assisted Hot Pressed sintering and conventional solution treatment

Study on the Selective Laser Melting of CuSn 10 Powder.

Selective laser melting of Cu–Cr–Zr copper alloy: Parameter optimization, microstructure and mechanical properties

Enhanced hardness and moderate thermal conductivity of Cu-2.4Ni-0.7Si alloy processed via selective laser melting followed by suitable heat treatment

Selective Laser Melting of High Relative Density and High Strength Parts Made of Minor Surface Oxidation Treated Pure Copper Powder

Effects of Low-Temperature Heat Treatment on Mechanical and Thermophysical Properties of Cu-10Sn Alloys Fabricated by Laser Powder Bed Fusion

Regulating the Microstructure and Mechanical Properties in Cast Al–3Li–2Cu-0.15Zr Alloy Via Sn Addition and Heat Treatment

Selective Laser Melting of Al-Zn-Mg-Cu: Heat Treatment, Microstructure and Mechanical Properties

Effect of Process Parameters on the Microstructure and Properties of Cu–Cr–Nb–Ti Alloy Manufactured by Selective Laser Melting

Microstructures and mechanical properties of Cu-Sn alloy subjected to elevated-temperature heat deformation

Selective laser melting 316L/CuSn10 multi-materials: Processing optimization, interfacial characterization and mechanical property

The mechanical and functional behaviors of Mn–15 wt.%Cu alloy produced by selective laser melting

Selective laser melting of CuCrZr alloy: processing optimisation, microstructure and mechanical properties

Revealing the Effect of Phase Composition and Transformation on the Mechanical Properties of a Cu–6Ni–6Sn–0.6Si Alloy

Effect of slight Sn modification on mechanical properties and corrosion behavior of Ti- (2–4 wt%) Mn alloys fabricated via powder metallurgy

The Influence of Heat Treatment on Microstructure and Properties of Selective Laser Melting CuCrZr Alloy