Perovskite ink with wide processing window for scalable high-efficiency solar cells

Mengjin Yang,Zhen Li,Matthew O. Reese,Obadiah G. Reid,Dong Hoe Kim,Sebastian Siol,Talysa R. Klein,Yanfa Yan,Joseph J. Berry,Maikel F. A. M. van Hest,Kai Zhu

DOI: https://doi.org/10.1038/nenergy.2017.38

IF: 56.7

2017-03-20

Nature Energy

Abstract:Perovskite solar cells have made tremendous progress using laboratory-scale spin-coating methods in the past few years owing to advances in controls of perovskite film deposition. However, devices made via scalable methods are still lagging behind state-of-the-art spin-coated devices because of the complicated nature of perovskite crystallization from a precursor state. Here we demonstrate a chlorine-containing methylammonium lead iodide precursor formulation along with solvent tuning to enable a wide precursor-processing window (up to ∼8 min) and a rapid grain growth rate (as short as ∼1 min). Coupled with antisolvent extraction, this precursor ink delivers high-quality perovskite films with large-scale uniformity. The ink can be used by both spin-coating and blade-coating methods with indistinguishable film morphology and device performance. Using a blade-coated absorber, devices with 0.12-cm2 and 1.2-cm2 areas yield average efficiencies of 18.55% and 17.33%, respectively. We further demonstrate a 12.6-cm2 four-cell module (88% geometric fill factor) with 13.3% stabilized active-area efficiency output.

materials science, multidisciplinary,energy & fuels