Highly Reproducible Fabrication of Perovskite Films with an Ultrawide Antisolvent Dripping Window for Large‐Scale Flexible Solar Cells

Xiangyu Kong,Yue Jiang,Zhuoxi Li,Youshuang Zhou,Zhengjie Xu,Chen Cong,Xingsen Gao,Xubing Lu,Guofu Zhou,Jun-Ming Liu,Krzysztof Kempa,Jinwei Gao

DOI: https://doi.org/10.1002/solr.202000646

IF: 9.1726

2020-12-04

Solar RRL

Abstract:Although perovskite solar cells (PSCs) have exhibited a high‐power conversion efficiency, the reproducibility of high‐quality perovskite films is still a big challenge for large‐scale flexible devices. One reason is the super narrow antisolvent dripping window, the other one is the difficulty in controlling the secondary phases. Herein, 18C6 is introduced into the perovskite precursor to achieve a high‐quality and reproducible large‐scale (7 × 7 cm2) flexible perovskite film by enlarging the antisolvent dripping window from 2 to 20 s, with an average efficiency of 13.33% (best 15.80%). Moreover, from the in situ grazing‐incidence wide‐angle X‐ray scattering result, the 2H phase perovskite is highly suppressed with the additive of 18C6. The generality of the approach is also demonstrated in other antisolvents such as ethyl acetate. This finding provides an innovative solution to the realization of repeatable, large‐scale solution fabrication of PSCs. A small molecule of 18C6 is introduced into the perovskite precursor for elongating the antisolvent dripping window from 2 to 20 s, achieving a high‐quality and reproducible perovskite film.

energy & fuels,materials science, multidisciplinary

What problem does this paper attempt to address?

The main problem that this paper attempts to solve is to improve the repeatable preparation of high - quality perovskite films in large - scale flexible devices of perovskite solar cells (PSCs). Specifically, the researchers introduced 18 - crown - 6 (18C6) as an additive into the tricationic perovskite precursor solution to significantly widen the antisolvent dripping window, from the original 2 seconds to 20 seconds, and simultaneously suppress the formation of secondary phases. This method not only improves the fault - tolerance rate of operation but also makes it possible to prepare high - quality perovskite films within a wider time range, thereby enhancing the stability and performance of the device.

Through this method, the researchers achieved the successful preparation of large - area (7×7 cm²) flexible perovskite solar cell modules, with an average efficiency of 13.33% (up to 15.80%). This provides an efficient method for the large - scale manufacturing of perovskite - based photovoltaic devices and promotes the further development of this field.