CO–H2 Gas-Based Reduction Behavior of Cr-Rich Electroplating Sludge Mixed with Iron Ore Powder

Jian Zhang,Zhiwei Peng,Lingyun Yi,Mingjun Rao

DOI: https://doi.org/10.3390/met14030325

IF: 2.695

2024-03-13

Metals

Abstract:Cr-rich electroplating sludge (CRES) is a complicated solid waste with high contents of chromium and iron. It can be used as a main feed of the FINEX ironmaking process, which requires gas-based reduction before smelting reduction to produce molten iron with the proper addition of iron ore powder. In this study, the CO–H2 gas-based reduction behavior of CRES mixed with iron ore powder was evaluated between 700 °C and 850 °C, with a focus on the variations of key components containing Fe, Cr, and S with reduction temperature and time. It was found that the iron oxides in CRES had stepwise conversions to metallic iron as the reduction reaction proceeded. The iron metallization degree of the mixture of CRES and iron ore powder increased obviously below 750 °C and then grew minorly with the further increase of temperature. Moreover, this index varied similarly with an extension of reduction time up to 80 min. After reduction at 750 °C for 60 min with the volume concentration of H2 of 30% and flow rate of 160 mL/min, the iron metallization degree reached 79.08%. The rate in the process was limited by a chemical reaction with an activation energy of 41.32 kJ/mol. Along with the stepwise reduction of iron oxides to metallic iron, the chromium hydroxide and sulfates in CRES were reduced to Cr2O3 and sulfites and sulfides, respectively.

materials science, multidisciplinary,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the behavioral characteristics of chromium - rich electroplating sludge (CRES) mixed with iron ore powder during the CO - H₂ gas reduction process. Specifically, the study focuses on the changes of key components such as iron (Fe), chromium (Cr) and sulfur (S) during the reduction process in the temperature range from 700 °C to 850 °C. The main purpose of the study is to evaluate the performance of this mixture during the reduction process, especially the variation law of the degree of iron metallization with temperature and time, as well as the kinetic characteristics of the reduction process. In addition, the processes of chromium hydroxide and sulfate being converted into Cr₂O₃ and thiosulfate or sulfide during the reduction process are also explored.

Through this study, the authors hope to provide theoretical basis and technical support for the production of chromium - containing molten iron using CRES, and then replace high - carbon ferrochromium alloy for stainless steel manufacturing. This will not only contribute to the effective utilization of resources, but also reduce environmental pollution and improve the treatment efficiency of electroplating sludge.