Abstract:A comprehensive modeling framework for the thermoforming of polymer matrix woven laminate composite was developed. Two numerical indicators, the slip path length and traction magnitude, have been identified to be positively correlated to matrix smearing and wrinkling defects. The material model has been calibrated with picture-frame experimental results, and the prediction accuracy for intra-ply shear and thickness distribution was examined with measurements of the physically formed parts. Specifically, thickness prediction for most locations on the formed parts was accurate within an 11.6% error margin. However, at two points with significant intra-ply shear, the prediction errors increased to around 20%. Finally, a parametric study was conducted to determine the relationship between various process parameters and the quality of the formed part. For the trapezoidal part, orienting the laminate at 45 degrees to the mold axis reduces the likelihood of matrix smear and wrinkling defects. Although this laminate orientation yielded a greater spatial variation in part thickness, the thickness deviation is lower than that for the 0-degree orientation case. Two forming analyses were conducted with ramp rates of 25 mm/s and 80 mm/s to match the equipment's operational limits. It was observed that higher forming rates led to a greater likelihood of defects, as evidenced by a 15% and 10% increase in the formed part areas with longer slip paths and higher traction magnitudes, respectively. It was discovered that shallower molds benefit from faster ramp rates, while deeper molds require slower rates to manage extensive shearing, stretching and bending. Faster forming rates lead to smaller thickness increases at high intra-ply shear regions, indicating a shift from intra-ply shear to out-of-plane bending due to the visco-plastic effect of the molten laminate and can negatively impact part quality. Lastly, it was shown that a well-conceived strategy using darts could improve the part quality by reducing the magnitude of the defect indicators.

Performance of additively manufactured composite mold with uniform fiber orientation

Spring-in behavior of woven carbon fiber/polycarbonate thermoplastic composites

Additively Manufactured Carbon Fiber- Reinforced Thermoplastic Composite Mold Plates for Injection Molding Process

Modeling on the Effect of Automated Fiber Placement Induced Gaps in Curved Composite Laminates

Design and manufacture of mould-free fibre-reinforced laminates with compound curvature

Complex angle part fabricated by vacuum bag only process with interleaved dry fiber and prepreg

Mold Development for Resin Transfer Molding with Dimension Variation and Deformation Compensation

Process-Structure Coupled Simulation of Additive Manufactured Components

Experimental and numerical analysis of the consolidation process for additive manufactured continuous carbon fiber-reinforced polyamide 12 composites

Additive Manufacturing of Composite Polymers: Thermomechanical FEA and Experimental Study

Stress-adapted fiber orientation along the principal stress directions for continuous fiber-reinforced material extrusion

Full‐field effect of flow‐induced fiber orientation during compression molding of carbon fiber sheet molding compounds

Characteristics of in-situ automated fiber placement carbon-fiber-reinforced low-melt polyaryl ether ketone laminates part 1: Manufacturing influences

A study on interactive fiber rubber composite structures subjected to bend-twist coupling

A Modeling Framework for the Thermoforming of Carbon Fiber Reinforced Thermoplastic Composites

Integrated computational modeling of large format additive manufacturing: Developing a digital twin for material extrusion with carbon fiber-reinforced acrylonitrile butadiene styrene

Structure Design on Thermoplastic Composites Considering Forming Effects

Experimental and numerical analysis of new thermoplastic composite mandrels

Anisotropy and deformation heterogeneity in additive manufactured carbon-reinforced PEEK

Research into Specific Mechanical Properties of Composites Produced by 3D-Printing Additive Continuous-Fiber Fabrication Technology

The use of discontinuous PEEK/carbon fiber thermoplastic moulding compounds for thick-section componentry