Abstract:Graphitized carbon blacks have shown a more promising electrochemical performance than the non-treated ones when being applied in small amounts as conductive additives in composite cathode electrodes for lithium ion batteries, due to the absence of surface functional groups which contribute to detrimental side-reactions with the electrolyte. Here, we report that at high potentials of >4.5 V vs. Li/Li(+), graphitic structures in carbon black can provide host sites for the partially reversible intercalation of electrolyte salt anions. This process is in analogy to the charge reaction of graphite positive electrodes in dual-ion cells. A standard furnace carbon black with small graphitic structural units, as well as slightly and highly graphitized carbon blacks, were characterized and analyzed with regard to anion intercalation. A LiPF6 containing organic solvent based electrolyte as well as a state-of-the-art ionic liquid based electrolyte composed of LiTFSI in PYR14TFSI were applied. The intercalation of both PF6(-) and TFSI(-) could be confirmed by cyclic voltammetry in electrodes made of carbon blacks. When exposed to high potentials, carbon blacks experienced strong activation in the 1st cycle, which promotes the perception for anion intercalation, and thus increases the anion intercalation capacity in the following cycles. The specific capacity from anion intercalation was evaluated by constant current charge-discharge cycling. The obtained capacity was proportional to the graphitization degree. As anion intercalation might be accompanied by decomposition reactions of the electrolyte, e.g., by co-intercalation of solvent molecules, it could induce the decomposition of the electrolyte inside the carbon and thus degradation of the carbon black graphitic structure. In order to avoid side reactions from surface groups and from anion intercalation, the thermal treatment of carbon blacks must be optimized.

Anion Intercalation into Graphite Electrode from Ethylene Carbonate Solutions Dissolving both Lithium Hexafluorophosphate and Lithium Bis(trifluoromethanesulfonyl)imide

Unraveling the Irreversible Storage of Dimethyl Carbonate-Solvated Hexafluorophosphate Anions in Graphite Electrode.

Combining Experiments and Theoretical Calculations to Investigate the Intercalation Behavior of Bis(trifluoromethanesulfonimide) Anion into Graphite Electrodes from Alkyl Phosphates

Intercalation of Tetrafluoroborate Anions into Graphite Electrodes from Mixed Sulfones

Electrochemistry-Driven Interphase Doubly Protects Graphite Cathodes for Ultralong Life and Fast Charge of Dual-Ion Batteries.

Intercalation Behavior of Tetrafluoroborate Anion in a Graphite Electrode from Mixed Cyclic Carbonates

Interplay among Hexafluorophosphate, Difluoro(oxalato)borate Anions and Ethylene Carbonate during Their Insertion into a Graphite Electrode

Cooperation of Dimethyl and Diethyl Carbonates in Hexafluorophosphate Anion Intercalation into Graphite Electrode

Anion Storage Behavior of Graphite Electrodes in LiBF4/Sulfone/Ethyl Methyl Carbonate Solutions

Partially Fluorinated Ether As an Electrolyte Additive to Modify Electrode Surface and Suppress Dissolution of Polysulfides in Li-S Batteries

PF6 − Intercalation into Graphite Electrode from Gamma-butyrolactone/ethyl Methyl Carbonate

Hexafluorophosphate Intercalation into Graphite Electrode from Propylene Carbonate/methyl Acetate Solutions

Balancing salt concentration and fluorinated cosolvent for graphite cathode-based dual-ion batteries

Hexafluorophosphate Anion Intercalation into Graphite Electrodes from Propylene Carbonate/Gamma-Butyrolactone Solutions.

Hexafluorophosphate Intercalation into the Graphite Electrode from Mixed Cyclic Carbonates

Investigation of PF6(-) and TFSI(-) anion intercalation into graphitized carbon blacks and its influence on high voltage lithium ion batteries

Anion Intercalation into a Graphite Electrode from Trimethyl Phosphate

Tuning Electrolyte Solvation Structure and CEI Film to Enable Long Lasting FSI−‐Based Dual‐Ion Battery

Hexafluorophosphate anion intercalation into graphite electrode from sulfolane/ethylmethyl carbonate solutions

Inhibiting Solvent Co‐Intercalation in a Graphite Anode by a Localized High‐Concentration Electrolyte in Fast‐Charging Batteries

Solid Electrolyte Interphase (SEI) Formation on the Graphite Anode in Electrolytes Containing the Anion Receptor Tris(hexafluoroisopropyl)borate (THFIPB)