Xinlin Ma,Jin Liu,Jun Zhang,Yucai Su,Kangfeng Yi,Yanfei Zhang,Linfeng Ding,Qiuju Zheng
Abstract:Boroaluminosilicate (BAS) glasses have excellent chemical durability and mechanical properties and are widely used in the pharmaceutical packaging industry. The corrosion behavior of boroaluminosilicate (BAS) glasses have been investigated for many years; however, the impact of chemical corrosion on mechanical properties of boroaluminosilicate glasses has not been well understood. In this work, the BAS glass samples were corroded in a 20 mM Glycine–NaOH buffer solution (pH = 10) at 80 °C for various durations. Within the corrosion durations, the corrosion of the glass is dominated by congruent dissolution. The results show that the elemental composition and structure of the glass surface are not altered significantly during the congruent dissolution, and the corrosion rate is mainly affected by the Si concentration in the solution. The structural change in the process of micro-crack decay is the main factor affecting the mechanical properties of the glass surface. Corrosion leads to the growth of micro-cracks and tip passivation, which causes the hardness and elastic modulus of the glass to first decrease and then increase. As corrosion proceeds, the microcracks are completely destroyed to form micropores, and the pore size and number increase with the corrosion process, resulting in the decrease in surface mechanical properties again. This work reveals the main influencing factors of congruent dissolution on mechanical properties and provides an important reference for the improvement of pharmaceutical glass strength.
materials science, multidisciplinary,metallurgy & metallurgical engineering,physics, applied,chemistry, physical, condensed matter
What problem does this paper attempt to address?
The problem that this paper attempts to solve is the effect of chemical corrosion on the mechanical properties of medicinal borosilicate - aluminosilicate glass (BAS glass). Specifically, the research focuses on understanding how chemical corrosion changes the mechanical properties of these glasses during the congruent dissolution stage and exploring the mechanisms behind such changes.
### Problem Background
Medicinal glass plays a crucial role in the packaging of drugs and vaccines, especially during the global COVID - 19 pandemic when the demand for drugs and vaccines has increased dramatically. To ensure the quality, safety, and effectiveness of drugs, medicinal glass must possess high chemical stability and excellent mechanical properties. However, medicinal glass undergoes chemical corrosion during long - term contact with drugs, which affects its mechanical properties. Therefore, understanding the corrosion mechanism and its effect on mechanical properties is essential for improving the practical application performance of glass.
### Research Methods
The researchers selected commercial BAS medicinal glass as the research object and placed it in a 20 mM Glycine - NaOH buffer solution (pH = 10) for corrosion experiments at 80°C for different durations (0 to 384 hours). Through means such as weight loss rate, atomic force microscopy (AFM), Raman spectroscopy, time - of - flight secondary ion mass spectrometry (TOF - SIMS), and nano - indentation experiments, the changes in surface morphology, roughness, chemical structure, and mechanical properties during the corrosion process were systematically studied.
### Main Findings
1. **Weight Loss Rate**: As the corrosion time increases, the weight loss rate of the glass first increases rapidly and then gradually slows down. This is related to the increase in Si concentration in the solution, which reduces the dissolution rate of the glass network.
2. **Surface Morphology and Roughness**: In the early stage of corrosion, small undulations appear on the glass surface. As time passes, the surface roughness increases significantly, but the overall surface still remains relatively flat.
3. **Chemical Structure Changes**: The results of TOF - SIMS and Raman spectroscopy show that during the entire corrosion process, there are no significant changes in the element distribution and structure on the glass surface, indicating that the corrosion is mainly a congruent dissolution process.
4. **Mechanical Property Changes**: Corrosion causes the growth and tip blunting of micro - cracks, causing the hardness and elastic modulus of the glass to first decrease and then increase. As the corrosion continues, the micro - cracks are completely destroyed to form micropores, ultimately leading to another decrease in mechanical properties.
### Conclusion
This study shows that during the congruent dissolution stage, chemical corrosion has a significant impact on the mechanical properties of BAS medicinal glass. Corrosion causes the growth and blunting of micro - cracks, which in turn affects the hardness and elastic modulus. These findings provide an important reference for improving the mechanical properties of medicinal glass.
### Formula Representation
Some formulas and data involved in the paper can be summarized as follows:
- **Weight Loss Rate**:
\[
\text{Weight loss rate}=\frac{\Delta m}{m_0}
\]
where \(\Delta m\) is the mass loss and \(m_0\) is the initial mass.
- **Surface Roughness Parameters**:
- \(Rq\) (root - mean - square roughness)
- \(Ra\) (arithmetic average roughness)
- **Volume Changes in Nano - indentation Experiments**:
- \(V^+\) (pile - up volume)
- \(V^-\) (residual indentation volume)
These results are helpful for understanding the specific impact of corrosion on the mechanical properties of medicinal glass and provide a theoretical basis for improving the performance of medicinal glass.