Effect of Heat Treatment on the Microstructure and Micro-mechanical Behavior of Quenched Ti-6Al-4V Alloy
Xinkai Ma,Fuguo Li,Jinghui Li,Jun Cao,Pan Li,Junzhe Dong
DOI: https://doi.org/10.1007/s11665-015-1682-z
IF: 2.3
2015-01-01
Journal of Materials Engineering and Performance
Abstract:To determine the influence of the solution treatment temperature and holding time on the microstructure and micro-mechanical behavior of Ti-6Al-4V alloys, micro-indentation experiments were conducted at maximum loads of 3000, 3500, 4500, 4600, 4700, 4800, and 4900 mN. A microstructure examination was also performed with an optical microscope. Based on the test data, the micro-hardness H , Young’s modulus E , yield strength σ y , ultimate tensile strength σ b , and strain-hardening exponent n were obtained by the Oliver-Pharr method. It was found that the solution treatment temperature and holding time had a significant influence on the morphology, size, and volume fraction of the α and β phases. The equiaxed microstructure (obtained at 950 °C) exhibits a higher H , E , and σ b . In contrast, σ y shows a downward trend over the entire range of solution treatment temperatures. The influences of holding time on H , E , σ b , and σ y were also significant.