Abstract:The kinetics of the transformation of metallic Fe to the active Fe carbide phase at the start of the Fischer–Tropsch (FT) reaction were studied. The diffusion rates of C atoms going in or out of the lattice were determined using 13C-labeled synthesis gas in combination with measurements of the transient 12C and 13C contents in the carbide by temperature-programmed hydrogenation. In the initial 20 min, C diffuses rapidly into the lattice occupying thermodynamically very stable interstitial sites. The FT reaction starts already during these early stages of carburization. When reaching steady state, the diffusion rates of C in and out of the lattice converge and the FT reaction continues via two parallel reaction mechanisms. It appears that the two outer layers of the Fe carbide are involved in hydrocarbon formation via a slow Mars–Van Krevelen-like reaction contributing to ∼10% of the total activity, while the remainder of the activity stems from a fast Langmuir–Hinshelwood reaction occurring over a minor part of the catalyst surface.

What problem does this paper attempt to address?

The problem that this paper attempts to solve is related to the carbonization process of iron - based catalysts in the Fischer - Tropsch (FT) reaction and its impact on the FT reaction activity. Specifically, through isotope exchange experiments, the researchers explored the kinetic process of the transformation of metallic iron into the active iron carbide phase, as well as the diffusion rate and mechanism of carbon atoms in the lattice during this process. The research focuses on: 1. **Kinetics of Iron Carbide Formation**: Study the kinetic process in the initial stage of the transformation of iron from the metallic state to the active iron carbide phase. In particular, at the beginning of the FT reaction, how carbon atoms rapidly diffuse into the iron lattice and occupy the thermodynamically very stable interstitial positions. 2. **Diffusion Mechanism of Carbon Atoms**: By using labeled syngas (containing $^{13}C$) and combining with the temperature - programmed hydrogenation (TPH) measurement technique, determine the diffusion rate of carbon atoms in and out of the lattice. It was found that within the first 20 minutes, carbon atoms rapidly diffuse into the lattice, and when the steady state is reached, the diffusion rates of carbon atoms in and out tend to be the same. 3. **Dual - Parallel Mechanism of the FT Reaction**: The research reveals that under steady - state conditions, the FT reaction proceeds through two parallel reaction mechanisms. Among them, the outer two layers of the iron carbide participate in a slower Mars - Van Krevelen - like reaction, contributing about 10% of the total activity; while the remaining activity is derived from a faster Langmuir - Hinshelwood reaction, which mainly occurs in a small area on the catalyst surface. 4. **Dynamic Behavior of Carbon Atoms**: Through TPH analysis, the change of the distribution of carbon atoms in the bulk and on the surface of the iron carbide over time was studied, especially the exchange of $^{13}C$ and $^{12}C$. It was found that carbon atoms not only exchange dynamically in the bulk phase, but also can diffuse outward through the surface layer to replenish the surface carbon species. In summary, this paper aims to deeply understand the carbonization process of iron - based catalysts in the FT reaction and its impact on the reaction activity, especially the dynamic behavior of carbon atoms in the catalyst bulk and on the surface, which is of great significance for optimizing the design of catalysts and improving the efficiency of the FT reaction.

Isotopic Exchange Study on the Kinetics of Fe Carburization and the Mechanism of the Fischer–Tropsch Reaction

Influence of carbon deposits on Fe-carbide for the Fischer-Tropsch reaction

Recent Mechanistic Understanding of Fischer-Tropsch Synthesis on Fe-Carbide

Synthesis of Iron-Carbide Nanoparticles: Identification of the Active Phase and Mechanism of Fe-Based Fischer–Tropsch Synthesis

Spectroscopic and Transient Kinetic Studies of Site Requirements in Iron-Catalyzed Fischer−Tropsch Synthesis

A DFT study towards dynamic structures of iron and iron carbide and their effects on the activity of the Fischer–Tropsch process

The role of H2 in Fe carburization by CO in Fischer-Tropsch catalysts

Atomically Defined Iron Carbide Surface for Fischer–Tropsch Synthesis Catalysis

Preparation of Iron Carbides Formed by Iron Oxalate Carburization for Fischer–Tropsch Synthesis

In Situ Active Site for Fe-Catalyzed Fischer-Tropsch Synthesis: Recent Progress and Future Challenges

Mechanism of Cobalt-Catalyzed CO Hydrogenation: 2. Fischer–Tropsch Synthesis

A New Insight into Fischer-Tropsch Synthesis

Computational investigation of the kinetics and mechanism of the initial steps of the Fischer-Tropsch synthesis on cobalt.

Carburized cobalt catalyst for the Fischer–Tropsch synthesis

Facet sensitivity of iron carbides in Fischer-Tropsch synthesis

Single-Phase θ-Fe3C Derived from Prussian Blue and Its Catalytic Application in Fischer-Tropsch Synthesis

The application of DFT calculation in the study of iron-based catalyst for Fischer-Tropsch synthesis

Molecular Views on Fischer-Tropsch Synthesis.

CO activation pathways and the mechanism of Fischer–Tropsch synthesis

Supported Fe2C catalysts originated from Fe2N phase and active for Fischer-Tropsch synthesis

Fischer-Tropsch Synthesis on Fe-Co-Pt/γ-Al2O3 catalyst: A mass transfer, kinetic and mechanistic study