Microstructure evolution and strengthening mechanism of CoCrFeMnNi HEA/Zr-3 brazed joints reinforced by fine-grained BCC HEA and HCP Zr
Xiaoguo Song,Nan Jiang,Hong Bian,Hyoung Seop Kim,Danyang Lin,Weimin Long,Sujuan Zhong,Lianhui Jia,Daijun Hu
DOI: https://doi.org/10.1016/j.jmst.2023.10.044
2023-12-17
Abstract:In the pursuit of manufacturing intricate components for the nuclear industry, we developed a novel Zr63.2Cu36.8 (wt.%) alloy via vacuum melting for brazing applications involving equiatomic high-entropy alloys (HEA) of CoCrFeMnNi and zircaloy (Zr-3). We systematically investigated the influence of various brazing parameters on microstructure evolution and shear properties. Furthermore, we established a comprehensive understanding of the relationship between the lattice structure of interfacial products, residual stress, and fracture behavior in HEA/Zr-Cu/Zr-3 joints. Our findings revealed that under specific conditions (1010 °C for 10 min), the reaction products in HEA/Zr-Cu/Zr-3 joints consisted of lamellar HEAP/lamellar Zr(Cr,Mn) 2 , granular (Zr,Cu)/Zr 2 (Cu,Ni,Co,Fe), bulk Zr(Cr,Mn) 2 , and Zrss. With increasing temperature and prolonged holding time, the layered HEAP and Zr(Cr,Mn) 2 phases adjacent to the HEA substrates thickened, while the relative amounts of Zr 2 (Cu,Ni,Co,Fe) decreased, with a remarkable increase in ductile Zrss. Growth kinetics analysis of the reaction layer and EBSD analysis indicated that the HEAP phases exhibited a lower growth rate compared to the Zr(Cr,Mn) 2 layer during brazing, and both phases exhibited random grain orientations. Particularly noteworthy was the precipitation of (Zr,Cu) within the layered Zr(Cr,Mn) 2 , which increased and coarsened with higher temperatures and extended durations. Finite element analysis and TEM analysis revealed higher residual stresses at the non-coherent Zr(Cr,Mn) 2 /HEAP interface with a lattice mismatch of 40.6%. The body-centered cubic (BCC) structural HEAP, composed of fine grains, effectively mitigated the concentrated residual stresses due to its superior plasticity. Moreover, micro-nanoscale close-packed hexagonal (HCP) precipitates (Zr,Cu) were distributed within the brittle Zr(Cr,Mn) 2 phases, contributing to the overall strength improvement of the joints. Consequently, high-quality HEA/Zr-3 joints were achieved, featuring a maximum strength of 172.1 MPa, equivalent to approximately 62.6% of the yield strength of Zr-3. These results highlight the potential of Zr63.2Cu36.8 (wt.%) alloys in advanced brazing applications. Graphical abstract Download : Download high-res image (272KB) Download : Download full-size image