Simulation of temperature field and stress field of selective laser melting of multi-layer metal powder

Zhonghua Li,Shuai Yang,Bin Liu,Wenpeng Liu,Zezhou Kuai,Yunfei Nie

DOI: https://doi.org/10.1016/j.optlastec.2020.106782

2021-08-01

Abstract:<p>In this study, the temperature field and the stress field of a multilayer metal powder were investigated using the point exposure scanning mode. A three-dimensional thermo-structural coupling model was established by using the finite element method, and the multi-layer multi-track SLM process was simulated. The model considered the latent heat of phase change, physical parameters with temperature change, convective heat transfer, and so on. The temperature, molten pool and stress changes at different positions were analyzed, and finally the residual stress distribution of the model was obtained. The residual stress distribution on the upper surface of the SLM fabricating part under point exposure scanning had strong volatility, which was different from continuous exposure scanning. The maximum residual stress appeared at the end of the first track in the first layer. The reliability of the numerical simulation was verified by the size of the molten pool in the experiment.</p>

optics,physics, applied

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the simulation and analysis of the temperature field and stress field of multi - layer metal powders during the Selective Laser Melting (SLM) process. Specifically, the researchers focus on the temperature distribution, molten pool change, thermal stress evolution and residual stress distribution during the SLM manufacturing process under the point - exposure scanning mode. By establishing a three - dimensional thermo - structural coupling model, the researchers hope to gain an in - depth understanding of the temperature and stress changes inside the material during the SLM process, thereby providing a theoretical basis for optimizing SLM process parameters and improving the quality and performance of the formed parts.

### Main problems:
1. **Temperature distribution**: Research on the temperature distribution of multi - layer metal powders during the SLM process, especially the temperature change under the point - exposure scanning mode.
2. **Molten pool change**: Analyze the molten pool size at different positions and its change over time.
3. **Thermal stress evolution**: Explore the generation and evolution process of thermal stress during the SLM process.
4. **Residual stress distribution**: Research on the residual stress distribution of SLM - manufactured parts after cooling, especially the residual stress distribution on the upper surface.

### Research background:
- SLM technology is an additive manufacturing method that melts metal powders layer by layer through a high - energy laser beam to finally form three - dimensional solid parts.
- During the SLM process, due to the instantaneous heating and rapid cooling of the high - energy laser beam, very high temperature gradients and thermal stresses will be generated, resulting in problems such as shrinkage, cracks, delamination, fatigue failure and thermal deformation of the formed parts.
- Numerical simulation is an important means to study temperature change, residual stress distribution and crack formation during the SLM process, because experimental measurement is costly and difficult.

### Innovation points:
1. **Point - exposure scanning mode**: Adopt the point - exposure scanning mode instead of the continuous - exposure scanning mode.
2. **Heat source penetration depth**: Consider the penetration of the heat source in the depth direction.
3. **Material property conversion**: Consider the property conversion between powder and solid materials.
4. **Multi - layer and multi - track finite element model**: Establish a multi - layer and multi - track finite element model for predicting temperature distribution, molten pool size change, thermal stress evolution and residual stress distribution.

### Model verification:
- Verify the effectiveness of the finite element model by comparing the simulation results with the measurement results of the molten pool size in the experiment.

### Conclusion:
- Under the point - exposure scanning mode, the residual stress distribution on the upper surface of SLM - manufactured parts has strong fluctuations, which is different from that in the continuous - exposure scanning mode.
- The maximum residual stress appears at the end of the first track of the first layer.
- The simulation results are consistent with the experimental results, verifying the reliability of numerical simulation.