Abstract:<p>The focus of this work is to characterize the progressive damage and failure behavior of 2.5D woven alumina fiber reinforced silica ceramic matrix thin composite specimen under a planar tension-shear stress state. The tensile and shear stress-strain diagrams in the principal material coordinate system were obtained using the off-axis tension test with the digital image correlation technique. A mesoscale finite element model of the composite material was developed within the framework of continuum damage mechanics. The thickness effect on the macroscopic mechanical response was considered by removing the periodic boundary conditions along the thickness direction. The macroscopic stress-strain response given by the numerical model was validated by the experimental results. The interaction of the planar biaxial tension and shear stresses was taken into account in the model, quantified using a shear contribution coefficient in the modified 3D Hashin failure criterion. The results from the damage evolution analysis indicate that the linear tensile stress-strain response with a brittle fracture characteristic for the on-axis tension specimen is governed by the axial fiber bundle. The nonlinear tensile stress-strain response with the significantly reduced ultimate stress under biaxial tension and shear stress state results from multiple damages with evolution in both axial and transverse fiber bundles. Both the effective tensile modulus and the ultimate tensile strength increase with increasing the thickness of the specimen due to the increase of the fiber volume fraction. The strengthening induced by the size effect is less significant for the specimen under biaxial tension and shear stress state than that for the on-axis tension specimen owing to the involvement of shear response dominated by the matrix of the material. The results of this study provide new insight into the failure of 2.5D woven ceramic-based composite material, which contributes to the optimal design of the reusable thermal protection system structure.</p>

Influence of hierarchical porosity on the mechanical properties of porous woven composites under thermomechanical loading

Progressive failure analysis of 2D woven composites at the meso-micro scale

A micromechanical damage model for oxide/oxide ceramic matrix composites with hierarchical porosity under thermomechanical loading

An effective multiscale analysis for the mechanical properties of 3D braided composites considering pore defects

3D Orthogonal Woven Carbon/Carbon Composites: Micromechanical Modeling and Damage Analysis

A hierarchical multiscale model for the elastic-plastic damage behavior of 3D braided composites at high temperature

An Insight into the Mechanical Properties of Unidirectional C/C Composites Considering the Effect of Pore Microstructures via Numerical Calculation

Influence of Complex Geometries on Damage Tolerance of Porous Carbon Fiber Network

Meso-scale modeling and damage analysis of carbon/epoxy woven fabric composite under in-plane tension and compression loadings

Effects of various porosities on the damage evolution behavior of carbon fiber/epoxy composites using acoustic emission and micro-CT

Multiscale numerical investigation on failure behaviour of three-dimensional orthogonal woven carbon/carbon composites subjected to pin-loading

A new progressive damage model for predicting the tensile behavior of the three-dimensional woven carbon/carbon composites using micromechanics method

Experimental and numerical investigation of progressive damage and failure behavior for 2.5D woven alumina fiber/silica matrix composites under a complex in-plane stress state

Experimental investigation on the effects of fabric architectures on mechanical and damage behaviors of carbon/epoxy woven composites

The effect of interface properties on the mechanical behaviour of 3D braided composites under unidirectional tensile loading

A Comparative Study on the Mechanical Properties of Open-Hole Carbon Fiber-Reinforced Thermoplastic and Thermosetting Composite Materials

Micro-porosity As Damage Indicator for Characterizing Cyclic Thermal Shock-Induced Anisotropic Damage in Oxide/oxide Ceramic Matrix Composites

A hierarchical multiscale strategy for analyzing the impact response of 3D braided composites

Experimental and Multiscale Numerical Investigation on Failure Behavior of Satin Woven Carbon/carbon Composites Subjected to Pin-Loading

Mechanical behavior simulation of particulate-filled composite at meso-scale by numerical manifold method

Microstructural and damage parameter effect analysis on the failure mechanism of fibrous soft tissues with a structure-based unit cell model