Corrosion-Resistant Functional Diamond Coatings for Reliable Interfacing of Liquid Metals with Solid Metals

Stephan Handschuh-Wang,Tao Wang,Lifei Zhu,Yang Xu,Lei Huang,Tiansheng Gan,Yongbing Tang,Xuechang Zhou

DOI: https://doi.org/10.1021/acsami.0c09428

2020-08-12

Abstract:Gallium-based liquid metals (GLMs) exist as atypical liquid-phase metals at and near room temperature while being electrically and thermally conductive, enabling copious applications in soft electronics and thermal management systems. Yet, solid metals are affected by interfacing with GLMs, resulting in liquid metal embrittlement and device failure. To avert this issue, mechanically durable and electrically tunable diffusion barriers for long-term reliable liquid metal–solid metal interfacing based on the deposition of various diamond coatings are designed and synthesized, as they feature high chemical inertness and extraordinary mechanical resistance. The diamond coatings show superlyophobicity (GLM contact angle ≥ 155°) and are nonstick toward GLMs, thereby achieving high mobility of GLM droplets (sliding angle 8–12°). The excellent barrier and anti-adhesion performance of the diamond coatings are proven in long-term experiments (3 weeks) of coated titanium alloy (Ti) samples in contact with GLMs. The electrical performance of the conductive diamond coating deposited on Ti is reliable and stable over a period of 50 h. As proof-of-concept applications a switch and a thermal management device based on liquid metals are demonstrated, signifying that coating diamond films on metals is a potent means to achieve stable integration of solid metals with GLMs.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c09428?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c09428</a>.Droplet impact test of a LM droplet (release height 8 cm) on diamond-coated Ti with hierarchical roughness (Movie S1) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c09428/suppl_file/am0c09428_si_001.mp4">MP4</a>)Droplet impact test of a LM droplet (release height 8 cm) on BDD-coated Ti (Movie S2) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c09428/suppl_file/am0c09428_si_002.mp4">MP4</a>)Application of the diamond-coated Ti in a thermal management system; upper diamond-coated Ti sample was heated with a red laser while a video of the UV irradiation was captured; here, the applied compression force was 6.8 N (Movie S3) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c09428/suppl_file/am0c09428_si_003.mp4">MP4</a>)Application of the diamond-coated Ti in a thermal management system; upper diamond-coated Ti sample was heated with a red laser while a video of the UV irradiation was captured; here, the applied compression force was 0.45 N (Movie S4) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c09428/suppl_file/am0c09428_si_004.mp4">MP4</a>)Description of the synthesis of the various diamond coatings, water contact angle on a structured and flat boron-doped diamond coating, roll-off angle of liquid metal droplets, further droplet impact tests, EDS spectra of the titanium substrate After contact with Galinstan, optical photographs, and EDS spectra of the BDD-coated Ti sample after cleaning (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c09428/suppl_file/am0c09428_si_005.pdf">PDF</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology