Achieving high power density and excellent durability for high temperature proton exchange membrane fuel cells based on crosslinked branched polybenzimidazole and metal-organic frameworks

Yingnan Wu,Xiaoting Liu,Fan Yang,Leon Lee Zhou,Bibo Yin,Peng Wang,Lei Wang

DOI: https://doi.org/10.1016/j.memsci.2021.119288

IF: 9.5

2021-07-01

Journal of Membrane Science

Abstract:<p>The power density and durability of fuel cell strongly rely on the properties of high-temperature (100 °C–200 °C) proton exchange membranes (HT-PEMs). Phosphoric acid-doped polybenzimidazole (PA-PBI) membranes are one of the most promising materials for HT-PEMs. However, the performance and durability of PA-PBI membranes still need to be improved. In this work, crosslinked branched PBI was chosen as polymer matrix due to its excellent chemical stability and high conductivity. The metal-organic framework (MOF) UiO-66 was introduced to constructed proton transport channels in crosslinked branched PBI composite membranes. As a result, a high proton conductivity (0.100 S cm⁻¹) of the composite membrane at relatively low PA uptake (126%) was obtained and the long-term stability was improved significantly. The best peak power density of 607 mW cm⁻² at 160 °C under anhydrous conditions was achieved for the composite membrane-based MEA in a fuel cell test. The fuel cell exhibits excellent durability and only a slight decrease in the load voltage value (36.0 μV h⁻¹) is observed. These results indicate that introducing UiO-66 MOF into cross-linked branched PBI membranes may provide a valid method towards developing high-performance HT-PEMs.</p>

engineering, chemical,polymer science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is how to achieve high power density and excellent durability in high - temperature proton - exchange membrane fuel cells (HT - PEMFCs). Specifically, the research aims to improve the performance and durability of high - temperature proton - exchange membranes (HT - PEMs) by introducing metal - organic frameworks (MOFs) into cross - linked branched polybenzimidazole (PBI) composite membranes.

### Background and Problems
1. **Background**:
- High - temperature proton - exchange membrane fuel cells (HT - PEMFCs) have received extensive attention due to their high - efficiency energy conversion and environmental - friendly characteristics.
- Phosphoric acid - doped polybenzimidazole (PA - PBI) membranes are one of the most promising high - temperature proton - exchange membrane materials at present because they have good thermal and chemical stabilities under working conditions.
- However, the performance and durability of PA - PBI membranes still need to be further improved.

2. **Problems**:
- **Decline in mechanical properties**: A high phosphoric acid doping amount will lead to a decline in the mechanical properties of PA - PBI membranes, thus affecting their durability.
- **Phosphoric acid loss**: During the operation of fuel cells, excessive phosphoric acid is likely to escape from the membranes, further reducing the durability of the membranes.
- **Dependence on high phosphoric acid doping amount**: In order to obtain high proton conductivity, a high phosphoric acid doping amount is usually required, but this will bring about the above - mentioned problems.

### Solutions
1. **Cross - linked branched PBI**:
- By introducing a cross - linked branched structure, the free volume of PBI membranes can be increased, so as to maintain a high proton conductivity at a lower phosphoric acid doping amount.
- The cross - linked branched structure can also enhance the dimensional stability and antioxidant properties of the membranes.

2. **Introduction of MOFs**:
- Metal - organic frameworks (MOFs) have high porosity, large specific surface area and good chemical stability.
- By introducing MOFs, efficient proton transport channels can be constructed in the membranes, thereby reducing the dependence on a high phosphoric acid doping amount.
- The specifically selected MOF is UiO - 66, which has excellent thermal and chemical stabilities.

### Experimental Results
1. **Proton conductivity**:
- The composite membrane achieved a high proton conductivity (0.100 S cm⁻¹) at a lower phosphoric acid absorption rate (126%), which was significantly better than that of the pure cross - linked branched PBI membrane.
- As the MOF loading amount increased, the proton conductivity was further improved.

2. **Mechanical properties**:
- The mechanical properties of the cross - linked branched PBI membrane were better than those of the uncross - linked PBI membrane.
- After the introduction of MOFs, the mechanical properties of the membrane decreased to a certain extent, but still showed good performance at a high MOF loading amount.

3. **Phosphoric acid retention ability**:
- The cross - linked branched PBI membrane had a better phosphoric acid retention ability.
- After the introduction of MOFs, the phosphoric acid retention ability of the membrane was further enhanced.

4. **Fuel cell performance**:
- The fuel cell based on the composite membrane reached a peak power density of 607 mW cm⁻² under anhydrous conditions at 160 °C, which was significantly better than other reported high - temperature proton - exchange membranes.
- The composite membrane also showed excellent durability. During the 187 - hour test, the load voltage value only decreased by 36.0 μV h⁻¹.

### Conclusion
By introducing UiO - 66 MOFs into cross - linked branched PBI membranes, the key problems of high power density and excellent durability in high - temperature proton - exchange membrane fuel cells have been successfully solved. This method provides an effective way to develop high - performance high - temperature proton - exchange membranes.