Abstract:The localized increase in the salt concentration and higher rate of oxygen diffusion lead to enhanced pitting corrosion in wet‐dry salt spray corrosion condition. Higher pitting corrosion degraded the strength and elongation capacity of the material significantly by changing the mode of failure from ductile to mix mode. Highly formable interstitial‐free steel has been subjected to corrode in wet‐dry salt spray (WDSS) and immersion corrosion (IMCC) conditions in 5, 10, 20, 30, and 45 days to investigate its corrosion behavior in simulated‐marine environment at the same temperature using 5 wt.% NaCl. The corrosion mechanisms and their effects have been studied and compared on the basis of weight loss and mechanical properties. Results revealed that corrosion rate in WDSS is about 9.5 times higher than IMCC. The corrosion coefficient (n) values for WDSS and IMCC have been observed as 0.99 and 0.35, respectively, which are evident for the protective nature of rust. The corrosion mechanisms and rust constituents may attribute different corrosion kinetics in both conditions. Moreover, the rate of degradation in yield strength and fracture strain in WDSS is 2 and 2.5 times higher than IMCC respectively; however, in the case of ultimate tensile strength the degradation rate is nearly same. It has also been observed that the higher pitting corrosion in WDSS may lead to change the failure mode from ductile to mix‐mode after 30 and 45 days of corrosion as authenticated from scanning electron microscopic images.

Droplet size dependent localized corrosion evolution of M50 bearing steel in salt water contaminated lubricant oil

Study of the Corrosion Behaviors of M50 Steel in Brine-Contaminated Lubricating Oil

Study on Corrosion Behavior and First-Principle Analysis of M50 Steel in Lubricating Oil Contaminated by Salt Water

Evolution of Wetted and Corroded Areas on 8cr4mo4v Bearing Steel Exposed to Salt Water Contaminated Lubricant Oil

Spontaneous process of dispersed salt water droplets in lubricant oil establishing wetted areas: Settling, spreading, coalescing and de-wetting

Wide temperature range corrosion mechanism of M50 bearing steel in deteriorated oil-water mixture

Corrosion Assessment and Characterization of Aerospace-Bearing Steels in Seawater and Ester-Based Lubricants

Insight into the Triggering Effect of (al, Mg, Ca, Mn)-oxy-sulfide Inclusions on Localized Corrosion of Weathering Steel

Interaction of marine organisms on localized corrosion of 316L stainless steel in Dalian seawater

Insights into the Corrosion Mechanism of a 12cr F/M Steel in Oxygen-Saturated Liquid LBE

Mechanical and surface characterization of interstitial‐free steel corroded under wet‐dry salt spray and immersion conditions: A comparative study

Investigation of the Corrosion–Wear Interaction Behavior of 8Cr4Mo4V Bearing Steel at Various Corrosion Intervals

Effects of Surface Defects on Rolling Contact Fatigue of M50 Steel with Consideration to Both the Transgranular and Intergranular Damage

Corrosion behavior of low-alloy steel in tidal zone: A simulated investigation

Corrosion Analysis of Steels in Pot-bearings at Marine Atmosphere

Initiation and Propagation of Localized Corrosion Induced by (zr, Ti, Al)-O X Inclusions in Low-Alloy Steels in Marine Environment

Corrosion evolution and stress corrosion cracking behavior of a low carbon bainite steel in the marine environments: Effect of the marine zones

Study on corrosion, hydrogen permeation, and stress corrosion cracking behaviours of AISI 4135 steel in the tidal zone

Investigation on the initial atmospheric corrosion of mild steel in a simulated environment of industrial coastland by thin electrical resistance and electrochemical sensors

In-situ Characterization of Initial Marine Corrosion Induced by Rare-Earth Elements Modified Inclusions in Zr-Ti Deoxidized Low-Alloy Steels

Synergy of stress and corrosion in a 12Cr ferritic/martensitic steel exposed to static liquid lead-bismuth eutectic at 550°C