High-rate superplasticity in an equiatomic medium-entropy VCoNi alloy enabled through dynamic recrystallization of a duplex microstructure of ordered phases
Seok Su Sohn,Dong Geun Kim,Yong Hee Jo,Alisson Kwiatkowski da Silva,Wenjun Lu,Andrew John Breen,Baptiste Gault,Dirk Ponge
DOI: https://doi.org/10.1016/j.actamat.2020.03.048
IF: 9.4
2020-08-01
Acta Materialia
Abstract:<p>Superplasticity proceeds from fine-grained structures and requires high intrinsic resistance to grain growth at the deformation temperature. Here, we show that a mixture of two kinds of brittle ordered phases enables superplastic behavior through dynamic recrystallization in an equiatomic medium-entropy VCoNi alloy as a model material. The alloy annealed at 900°C exhibits a face-centered-cubic single phase. However, in-depth characterization at various length scales reveals that the alloy, when annealed at 800°C, comprises two ordered phases: κ (Co<sub>1.2</sub>Ni<sub>1.3</sub>V) and σ (Co<sub>1.5</sub>NiV<sub>2.5</sub>). As a result of the conventional cold-rolling/annealing process and with the aid of an underlying eutectoid reaction, the alloy exhibits a duplex structure with an average grain size of less than 1 μm, i.e. microduplex structure. The size, morphology, and crystallographic orientation do not substantially change during static isothermal holding at 800°C, which implies a very high resistance to grain growth. With tensile deformation at 800°C, however, both phases develop into an equiaxed microstructure with low dislocation density and a dramatic change occurs in the crystallographic texture of the κ phase. These variations result from dynamic recrystallization (DRX), which leads to superplastic elongations of 330–450% at 700–800°C and at strain rates ranging from 10<sup>–4</sup> to 10<sup>−2</sup> s<sup>−1</sup>. Notably, the superplastic behavior is favorable at the high strain rate due to the enhanced DRX activity, leading to the larger elongation with increasing strain rates. However, deformation-enhanced grain growth occurs concomitantly with dynamic recrystallization; these competitive processes are investigated to elucidate the mechanism of superplasticity in this model material.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering