Preparation and Characterization for the Thermal Stability and Mechanical Property of PLA and PLA/CF Samples Built by FFF Approach

Mengyu Cao,Tianqi Cui,Yuhang Yue,Chaoyu Li,Xue Guo,Xin Jia,Baojin Wang
DOI: https://doi.org/10.3390/ma16145023
IF: 3.4
2023-07-17
Materials
Abstract:Currently, the mechanical performances of polylactic acid (PLA) samples prepared using the fused filament fabrication (FFF) technique are relatively poor. Hence, the carbon fiber (CF) is used to improve the thermal stability and mechanical property of FFF-ed PLA samples in this paper. The crystalline structure, thermal stability, melt flow rate, tensile strength and fractured surface morphology of PLA and PLA/CF samples were investigated with an X-ray diffraction device, differential scanning calorimeter, thermogravimetric analyzer, melt flow rate equipment, universal tensile test machine and scanning electron microscope, respectively. Meanwhile, the reinforcement mechanism of CF on the mechanical property of PLA samples was also analyzed. XRD results revealed that the diffraction peaks intensities of PLA/CF sample were obviously lower than those of PLA sample. TGA and DSC curves illustrated that the initial thermal decomposition temperature, thermal stability and crystallinity of the PLA/CF sample improved significantly. The tensile strength of the PLA/CF sample was 91.58 MPa, which was 42.49% higher than that of the PLA sample. Moreover, SEM images showed that the fractured behavior of the PLA sample varied from brittle fracture to ductile fracture after the introduction of CF. The results concluded the CF is a feasible fiber for enhancing the performances of the PLA sample.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to prepare PLA and PLA/CF samples by adding carbon fiber (CF) to polylactic acid (PLA) materials and using fused filament fabrication (FFF) technology, in order to improve the thermal stability and mechanical properties of these samples. Specifically, the author studied the influence of CF on the crystalline structure, thermal stability, melt flow rate, tensile strength and fracture surface morphology of PLA samples, and analyzed the mechanism of CF - enhanced mechanical properties of PLA samples. The goal of the paper is to verify the effectiveness of carbon fiber as a reinforcing phase, improve the comprehensive performance of PLA samples prepared by the FFF process, and thus expand their application potential in fields such as automobiles, aerospace, education, medicine and mechanical engineering.