Abstract:Abstract GLARE laminates have emerged as a favored option for the construction of fuselage and wing skins in large airliners, owing to their exceptional mechanical characteristics. Nevertheless, the incorporation of open‐hole designs poses a challenge as it disrupts the continuity of the laminates, resulting in stress concentration and subsequent damage. To investigate the impact of various layup orientations and hole sizes on the tensile properties of open‐hole GLARE laminates, this study conducted axial tensile tests. Additionally, the tensile damage process was monitored using DIC and AE techniques, enabling the identification of damage patterns and the analysis of their evolution. The results demonstrate a noteworthy decline in the ultimate strength and failure strain as the size of the opening increases. Moreover, the retention rate of failure strain displays a marked sensitivity to the layup orientation. In conjunction with observations made through DIC and SEM, the k‐means++ algorithm successfully clustered peak frequencies, thereby revealing distinct damage patterns and their corresponding frequency ranges as aluminum alloy damage [0–90 kHz], matrix cracking [104–174 kHz], fiber/matrix debonding [175–224 kHz], interlaminar delamination [234–300 kHz], and fiber fracture [304–469 kHz]. AE cumulative counts were utilized to evaluate the progression of individual damage modes. The results emphasize that matrix cracking demonstrates the most substantial cumulative counts, whereas damage to the fibers and aluminum alloy noticeably affects the load‐carrying capability of the laminate. Furthermore, the fibers/matrix debonding and interlaminar delamination, exhibit heightened susceptibility to layup orientation and hole size. Highlights The tensile performance evaluation of GLARE laminates with open‐hole varying layup orientations and hole sizes was investigated. A combination of DIC and AE techniques was used to monitor the tensile damage process. Damage pattern was identified based on the observations of DIC and SEM. An approach based on Pearson's correlation coefficient and k‐means++ clustering algorithm was used for damage pattern recognition in GLARE laminates. AE cumulative counts were employed to assess the evolution of each damage mode.

Low-velocity impact (LVI) and post-impact fatigue properties of GLARE laminates with holes

Dynamic impact behavior and notched fatigue life of GLARE laminates

Soft Impact Response of Laminated Glass Plates

Delamination in GLARE laminates under low velocity impact

Energy dissipation mechanism of fiber metal laminate under low-velocity impact

Finite element analysis of dynamic progressive failure properties of GLARE hybrid laminates under low-velocity impact

Effect of symmetric and asymmetric aluminum arrangements on the low‐velocity impact performance of glass fiber‐reinforced aluminum laminate (GLARE)

Soft impact of GLARE fiber metal laminates

Characterizing damage patterns and evolution in Multi-Hole GLARE laminates under tensile load via integrated AE and DIC techniques

De Lamination And Fatigue Crack Growth Behavior In Fiber Metal Laminates (Glare) Under Single Overloads

Impact responses and residual flexural properties of narrow CFRP laminates

Effect of boundary conditions on the low‐velocity impact damage mechanism of fiber metal laminate

Experimental investigation on the compression‐after‐double‐impact behaviors of GFRP laminates embedded with aluminum mesh

Experimental study for the effect of hole notched in fracture mechanics of GLARE and GFRP composites subjected to quasi-static loading

Failures of laminates under nonpenetrative impacts

Short beam shear damage analysis of GLARE laminates based on digital image correlation and finite element analysis

Assessment of tensile damage mechanism of open‐hole GLARE laminates based on acoustic emission and digital image correlation techniques

Study of Low-Velocity Impact Behavior of Hybrid Fiber-Reinforced Metal Laminates

Notched behavior of hybrid glass/aluminum/titanium fiber metal laminates

On multiple low-velocity impact response and compression after impact of composite laminates

Progressive damage modelling and fatigue life prediction of Plain-weave composite laminates with Low-velocity impact damage