Effect of MT-technology of Heat Treatment on Reciproc: Comparison of Reciproc, Reciproc Blue and Reciproc MT

Zunduijamts Odgerel,Sang Won Kwak,Jung-Hong Ha,Gianluca Gambarini,Ya Shen,Hyeon-Cheol Kim

DOI: https://doi.org/10.1016/j.joen.2024.01.020

IF: 4.422

2024-02-04

Journal of Endodontics

Abstract:Introduction This study aimed to evaluate the effects from the memory-triple (MT) heat treatment on the fatigue resistance of the Reciproc by comparison to the file systems of same geometry. Methods Reciproc files subjected to MT heat treatment technology were designated as Group RMT were compared with the original Reciproc (Group REC) and Reciproc Blue (Group REB). Each NiTi file from three groups ( n = 15) was operated reciprocally with a repetitive up-and-down movement in the curved canal with a 4-mm of pecking distance inside of the simulated canal at body temperature. When each file fractured, the time until fracture was recorded. The length of the fractured fragment was measured. Fractured fragments were observed under scanning electron microscope (SEM) to evaluate the topographic features of the surface. Differential Scanning Calorimetry (DSC) analysis was performed to estimate phase transformation temperatures. One-way ANOVA and Duncan post-hoc comparison were applied to compare among the groups at a significance level of 95%. Results RMT showed significantly higher fracture resistance ( P < .05) while there was no difference in fatigue resistance between REC and REB. SEM examination showed the files from the 3 groups had similar topographic features. RMT showed a peak of austenite peak (A p ) at a temperature (52°C) higher than body temperature, while REC and REB showed A p at 37 and 32°C, respectively. Conclusions Under the condition of this study, the new heat treatment technique of MT technology could enhance the fatigue fracture resistance of the reciprocating files made of M-wire and Blue-wire.

dentistry, oral surgery & medicine