Abstract:This study aims to understand the water retention capabilities of Superabsorbent Polymers (SAPs) in different alkaline environments for internal curing and to assess their impact on the rheological properties of cement paste. Therefore, the focus of this paper is on the absorption capacities of two different sizes of polyacrylic-based Superabsorbent Polymers : SAP A, with an average size of 28 μm, and SAP B, with an average size of 80 μm, in various solutions, such as pH 7, pH 11, pH 13, and cement filtrate solution (pH 13.73). Additionally, the study investigates the rheological properties of SAP-modified cement pastes, considering three different water-to-cement (w/c) ratios (0.4, 0.5, and 0.6) and four different dosages of SAPs (0.2%, 0.3%, 0.4%, and 0.5% by weight of cement). The results showed that the absorption capacity of SAP A was higher in all solutions compared to SAP B. However, both SAPs exhibited lower absorption capacity and early desorption in the cement filtrate solution. In contrast to the absorption results in pH 13 and cement filtrate solutions, the rheological properties, including plastic viscosity and yield stress, of the cement paste with a w/c ratio of 0.4 and 0.5, as well as both dry and wet (presoaked) SAPs, were higher than those of the cement paste without SAP, indicating continuous absorption by SAP. The viscosity and yield stress increased over time with increasing SAP dosage. However, in the mixes with a w/c ratio of 0.6, the values of plastic viscosity and yield stress were initially lower for the mixes with dry SAPs compared to the reference mix. Additionally, cement pastes containing wet SAP showed higher viscosity and yield stress compared to the pastes containing dry SAP.

Impact of Superabsorbent Polymer on Shrinkage and Compressive Strength of Mortar and Concrete

The Influence of Nano-Silica Composite Superabsorbent Polymer on the Autogenous Shrinkage of Mortar

Effect of Superabsorbent Polymer (SAP) Size on Microstructure and Compressive Strength of Concrete

Hydration, Microstructure and Autogenous Shrinkage Behaviors of Cement Mortars by Addition of Superabsorbent Polymers

INFLUENCE OF SUPER ABSORBENT POLYMER ON DIMENSION SHRINKAGE AND MECHANICAL PROPERTIES OF CEMENT MORTAR

Effect of superabsorbent polymer on mechanical properties of cement stabilized base and its mechanism

Effect of Internal Pores Formed by a Superabsorbent Polymer on Durability and Drying Shrinkage of Concrete Specimens

Influence of Superplasticiser on Early Shrinkage and Total Shrinkage of Concrete

Influence of Superplasticizers on Early Age Drying Shrinkage of Cement Paste with the Same Consistency

Internal Relative Humidity, Autogenous Shrinkage, and Strength of Cement Mortar Modified with Superabsorbent Polymers

Influence of Superplasticizer Type and Dosage on Early-age Drying Shrinkage of Cement Paste with Consideration of Pore Size Distribution and Water Loss

Effects of kaolin-modified superabsorbent polymers on mortar properties

Effect of Super Absorbent Polymer mixing method on shrinkage performance of cast-in-place concrete confined by existing concrete

Effects on the Properties of Self-Compacting Cement Paste (PAA) with the Addition of Superabsorbent Polymer

Influence of Superabsorbent Polymer in Self-Compacting Mortar

Investigation of the Compressive Strength and Void Analysis of Cement Pastes with Superabsorbent Polymer

Effect of superabsorbent polymers (SAPs) and fly ash on mechanical properties and microstructure of mortar

Experimental Study of a Superabsorbent Polymer Hydrogel in an Alkali Environment and Its Effects on the Mechanical and Shrinkage Properties of Cement Mortars

Effect of Superabsorbent Polymer on the Mechanical Performance and Microstructure of Concrete

Delayed Absorption Superabsorbent Polymer for Strength Development in Concrete

Investigating the Impact of Superabsorbent Polymer Sizes on Absorption and Cement Paste Rheology