An in-depth insight at the percolation model and charge transport mechanism in La0.7Ca0.1Pb0.2Mn1-2xAlxSnxO3 manganite prepared by sol–gel route
khadija Dhahri,N. Dhahri,Souhir Bouzidi,Manel Hleili,Nuha Al-Harbi,N. M. Basfer,N. A. Harqani,J. Dhahri,P. Lachkar,E. K. Hlil
DOI: https://doi.org/10.1007/s10971-024-06438-1
2024-06-20
Journal of Sol-Gel Science and Technology
Abstract:In this work, we presented our results on the electrical and magnetoresistance characteristics of La 0.7 Ca 0.1 Pb 0.2 Mn 1-2x Al x Sn x O 3 (x equal to 0 and 0.025) prepared using the sol–gel method. X-ray diffraction (XRD) analysis revealed that all samples crystallize in Rhombohedral structure with R-3c space group. In addition, to obtain further information regarding the electrical properties, we performed resistance versus temperature ρ (T) measurements under different applied magnetic fields using a standard four-probe technique. The resistivity data, represented as ρ (μ 0 H, T), indicated the presence of a transition from metal to semiconductor state. As the magnetic field increases, the maximum resistivity values decrease, and the temperature (T M-SC ) at which the transition from insulator to metal occurs rises. In the temperature range where T is less than T M–SC , the electrical resistivity ρ (T) was modeled as ρ(T) = ρ 0 + ρ 2 T 2 + ρ 4.5 T 4.5 , signifying that the transport behavior is influenced by a combination of interactions involving electron–magnon, electron–phonon and electron–electron scattering processes. Conversely, in the temperature range exceeding T M–SC , the transport mechanism was elucidated through the utilization of adiabatic small polaron hopping and variable-range hopping models. To improve understanding of the variations in the resistivity profile across the temperature range, ρ (T) was fitted using the percolation model. Additionally, research was conducted on the magnetoresistance effect (MR %). The highest magnetoresistance values are observed around the temperature T M–SC .
materials science, ceramics