Abstract:A composite titania thin film consisted of quasi-aligned single-crystalline rutile nanorods embedded in sol-gel-derived anatase aggregates was fabricated and its photoelectrochemical behavior was studied in detail. A monolayer of nearly sing I e-crystal line rutile nanorods was first deposited on metallic Ti substrates through a controlled reaction between Ti and hydrogen peroxide. The gaps among the rutile nanorods were then filled with titania nanoparticles through a sol-gel dip-coating approach, which achieved a composite thin film of single-crystalline rutile nanorods embedded in anatase aggregates, after a subsequent thermal treatment at 723 K. The X-ray diffraction measurement revealed that the composite film with thickness of 180 nm contained anatase and rutile in a nearly 50:50 ratio. The UV-visible diffusive reflectance spectra estimated a band gap of 2.99 eV for the rutile monolayer and a slightly increased value of 3.03 eV for the composite film due to the embedding of the anatase nanoparticles. Photocurrent versus potential diagrams, photocurrent transient curves, and open-circuit potential measurement supported the fact that the anatase nanoparticles possessed better inherent photoelectrochemical properties than rutile. However, electrochemical impedance spectra characterization, together with photocurrent transient curves and open-circuit potential measurement, suggests that the single-crystalline rutile nanorods exhibited a higher electron-transfer rate. The combination of the two components in such an appropriate way enhanced significantly the charge separation effect arising from the anatase/rutile couple, which hence combined efficiently the "mixed crystal effect" and the "mixed morphological effect". A steady-state photocurrent more than double the simple sum of those generated by the two components alone was detected for the current composite film, which can be attributed to the single-crystalline rutile nanorods that provide channels for rapid electron transfer to the conductive Ti substrates under an applied bias potential. As a result, this study concludes that the present nanostructure magnified significantly the well-established mixed crystal effect, that is, an enhanced charge separation arising from a mixture of anatase and rutile.

Exploring the influencing factors of the electrochemical reduction process on the PEC water splitting performance of rutile TiO2

Single-crystalline Rutile TiO2 Nanorod Array on Flexible Ti Substrates for Efficient Photoelectrocatalytic Degradation of Phenol in Water

Surface Polaron States on Single-Crystal Rutile TiO2 Nanorod Arrays Enhancing Charge Separation and Transfer

Significantly Enhanced Visible Light Photoelectrochemical Activity in TiO2 Nanowire Arrays by Nitrogen Implantation

An effective strategy for promoting charge separation by integrating heterojunctions and multiple homojunctions in TiO2 nanorods to enhance photoelectrochemical oxygen evolution

Photoelectrocatalytic Efficiency of Low-Temperature Precipitated Monolayer Rutile TiO 2 Nanoflower Film

Enhanced Photoelectrochemical Response of a Composite Titania Thin Film with Single-Crystalline Rutile Nanorods Embedded in Anatase Aggregates

Balsam-Pear-Like Rutile/Anatase Core/Shell Titania Nanorod Arrays For Photoelectrochemical Water Splitting

Reversible Chemical Tuning of Charge Carriers for Enhanced Photoelectrochemical Conversion and Probing of Living Cells

Enhanced photoelectrocatalysis in porous single crystalline rutile titanium dioxide electrodes

Regulating Phase Junction and Oxygen Vacancies of TiO2 Nanoarrays for Boosted Photoelectrochemical Water Oxidation

Understanding the enhanced photoelectrochemical water oxidation over Ti-doped α-Fe 2 O 3 electrodes by electrochemical reduction pretreatment.

Selective Doping of Titanium into Double Layered Hematite Nanorod Arrays for Improved Photoelectrochemical Water Splitting

Surface engineering of hematite nanorods by 2D Ti3C2-MXene: Suppressing the electron-hole recombination for enhanced photoelectrochemical performance

Enhancing the photoelectrochemical performance of TiO2 photoanode by employing carbon nanoparticles as electron reservoirs and photothermal materials

Surface States As Electron Transfer Pathway Enhanced Charge Separation in TiO2 Nanotube Water Splitting Photoanodes

Photoelectrochemical performance enhancement of low-energy Ar+ irradiation modified TiO2

Insights into Improving Photoelectrochemical Water‐Splitting Performance Using Hematite Anode

Enhanced photoelectrochemical performance of NiS-modified TiO 2 nanorods with a surface charge accumulation facet

Influence of the electronic structures on the heterogeneous photoelectrocatalytic performance of Ti/RuxSn1-xO2 electrodes

Factors influencing the photocatalytic activity of rutile TiO2 nanorods with different aspect ratios for dye degradation and Cr(VI) photoreduction