Paraelectric Matrix-Tuned Energy Storage in BiFeO 3 –BaTiO 3 –SrTiO 3 Relaxor Ferroelectrics

Wei Wang,Ke Meng,Peng-Zu Ge,Xin-Gui Tang,Qiu-Xiang Liu,Yan-Ping Jiang

DOI: https://doi.org/10.1021/acsaem.1c01474

IF: 6.4

2021-08-18

ACS Applied Energy Materials

Abstract:Incorporation of polymorphic ferroelectric nanodomains into a paraelectric matrix has been proven to be effective to achieve high energy storage density in a relaxor ferroelectric system. In this work, we fabricated short-range ordered polymorphic 0.20BiFeO3–(0.80 – x)BaTiO3 nanodomains in a paraelectric xSrTiO3 host (0.40 ≤ x ≤ 0.65) to form ternary relaxors with transition temperatures in the range of 425–460 °C. The addition of SrTiO3 suppresses the P–E loops of the binary BiFeO3–BaTiO3 system and improves the recoverable energy and energy storage efficiency. A well-sintered solid solution exhibits nearly ideal relaxor ferroelectric behavior for x = 0.50, which demonstrates the highest tetrahedral c/a ratio (1.0042), saturation polarization (26.39 μC/cm2), breakdown strength (183.1 kV/cm), and recoverable energy (2.15 J/cm3 at 190 kV/cm) and also shows high current density, high power density, and short discharge time. The overall evolution of the c/a ratio, saturation polarization, and recoverable energy follows an x-dependent volcanic shape, while the variation of residual polarization is x-independent. The maximum energy storage efficiency of 95.56% is observed for x = 0.55 at 200 kV/cm. These findings suggested that the 0.20BiFeO3–(0.80 – x)BaTiO3–xSrTiO3 system is promising for dielectric energy storage applications.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsaem.1c01474.Comparison of the properties of our results with other BFO–BTO-based systems (Table S1) and supplementary references (PDF)This article has not yet been cited by other publications.

materials science, multidisciplinary,chemistry, physical,energy & fuels