Synergistically Improving Flexibility and Thermoelectric Performance of Composite Yarn by Continuous Ultrathin PEDOT:PSS/DMSO/Ionic Liquid Coating
Mufang Li,Fanjia Zeng,Mengying Luo,Xing Qing,Wen Wang,Ying Lu,Weibing Zhong,Liyan Yang,Qiongzhen Liu,Yuedan Wang,Jie Luo,Dong Wang
DOI: https://doi.org/10.1021/acsami.1c15946
2021-10-14
Abstract:Combining fabrics with a poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) coating is the most promising method to fabricate wearable thermoelectric (TE) devices. However, the high modulus, low strain, and low TE performance of PEDOT:PSS coating lead to poor flexibility and low power generation efficiency. In this study, dimethyl sulfoxide (DMSO) and ionic liquids (ILs) were selected as a modifier to enhance the flexibility and TE performance of PEDOT:PSS. Different from the penetrating structure and coil conformation of pristine PEDOT:PSS coating, a flexible continuous ultrathin layer of PEDOT:PSS/DMSO/1-ethyl-3-methylimidazolium dicyanamide (P/D/ED) with a linear conformation forms on the surface of cotton yarn. The morphology and structure of PEDOT:PSS and P/D/ED coating were characterized by FESEM, XPS, and Raman spectroscopy. Compared with the pristine PEDOT:PSS film, the P/D/ED film shows significantly reduced modules and enhanced strain and bending stability. Moreover, the TE performance of P/D/ED-coated yarn is significantly enhanced with nearly half mass loading. Based on this, a large-area wearable TE fabric with enhanced flexibility and TE performance was prepared. The output power density is 136.1 mW/m2 at ΔT = 40.8 K, which is a typically high value compared with the former reported composite TE fabrics. This study provides a new way to synergistically enhance the flexibility and TE performance of composite yarn, and the prepared TE fabric has great potential as a wearable power source.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c15946.Fabrication process of the composite TE yarn and TE fabric; morphology of the 4# yarn, P/D-coated yarn, and P/D/ED-coated yarn; water contact angle of the P/D film, P/D-coated yarn, P/D/ED-film, and P/D/ED-coated yarn; elemental distribution mapping of P/D and P/D/ED; structure of the TE fabric; temperature difference between the two ends of TE yarns with different lengths; comparison of the output power density obtained in this study and the previously reported textile-based TE generator (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology