Highly conductive, ultra-flexible and continuously processable PEDOT:PSS fibers with high thermoelectric properties for wearable energy harvesting

Ningxuan Wen,Zeng Fan,Shuaitao Yang,Yongpeng Zhao,Tianze Cong,Shihong Xu,Hao Zhang,Jianzhen Wang,Hui Huang,Chengwei Li,Lujun Pan
DOI: https://doi.org/10.1016/j.nanoen.2020.105361
IF: 17.6
2020-12-01
Nano Energy
Abstract:<p>Conducting polymers, particularly poly (3,4-ethylenedioxythiophene): poly (styrenesulfonate) (PEDOT:PSS), have been intensively studied for thermoelectric (TE) applications, owing to their unique advantages including nontoxicity, low cost, good mechanical flexibility and low thermal conductivity. The TE properties of the conducting polymers show a strong dependence on their polymer chain conformations and chain stacking structures. In this work, one-dimensional PEDOT:PSS fibers were developed to improve the chain packing order and increase the proportions of quinoid PEDOT by the spatial confinement effect arising from the specific fiber configuration. The PEDOT:PSS fibers were produced through a continuous wet-spinning process followed by a one-step treatment with sulfuric acid. The optimized PEDOT:PSS fibers achieved a power factor of 147.8 μW m<sup>−1</sup> K<sup>−2</sup> with an electrical conductivity of 4029.5 S cm<sup>−1</sup> and a Seebeck coefficient of 19.2 μV K<sup>−1</sup> at room temperature. The power factor was 15 times that of a two-dimensional PEDOT:PSS film processed at the same condition. Besides, the PEDOT:PSS fibers also exhibited a high tensile strength of 389.5 MPa and a large breaking strain of 30.5%. Based on the PEDOT:PSS fibers, a prototype fibrous TE generator (TEG) was assembled. The fibrous TEG delivered an output power density of ~0.273 μW cm<sup>−2</sup> using the human body heat. This work paves the way to developing high-performance organic TE materials by approaches of polymer chain modulation.</p>
materials science, multidisciplinary,chemistry, physical,physics, applied,nanoscience & nanotechnology
What problem does this paper attempt to address?
The main problem that this paper attempts to solve is to improve the performance of organic thermoelectric materials, especially by developing PEDOT:PSS fibers with high conductivity, super - flexibility and continuous processability to achieve efficient wearable energy harvesting. Specifically, the authors aim to improve the thermoelectric performance of PEDOT:PSS materials in the following aspects: 1. **Optimizing polymer chain arrangement and stacking structure**: Through the space - confinement effect of one - dimensional fiber configuration, the arrangement order of PEDOT:PSS chains is improved, and the proportion of quinoid - PEDOT is increased, thereby enhancing the thermoelectric performance of the material. 2. **Developing continuous wet - spinning process**: High - performance PEDOT:PSS fibers are prepared by using continuous wet - spinning technology combined with sulfuric acid post - treatment. This process can be produced on a large scale and can effectively regulate the physical and chemical properties of the fibers. 3. **Improving mechanical properties**: Ensure that the fibers not only have excellent thermoelectric properties, but also have high tensile strength and large fracture strain, making them suitable for complex structural design and practical applications. 4. **Verifying practical application potential**: Based on the prepared PEDOT:PSS fibers, a prototype fibrous thermoelectric generator (TEG) is assembled and its application potential as a wearable device is demonstrated. ### Key Results - **Significant improvement in power factor (PF)**: The optimized PEDOT:PSS fibers achieve a power factor of 147.8 μW m⁻¹ K⁻² at room temperature, which is 15 times higher than that of two - dimensional PEDOT:PSS films treated under the same conditions. - **Electrical conductivity and Seebeck coefficient**: The electrical conductivity of the fibers is 4029.5 S cm⁻¹, and the Seebeck coefficient is 19.2 μV K⁻¹. - **Superior mechanical properties**: The fibers exhibit extremely high tensile strength (389.5 MPa) and large fracture strain (30.5%). - **Demonstration of practical applications**: Using 5 pairs of PEDOT:PSS fibers and nickel wires as p - type and n - type thermoelectric legs, the assembled fibrous thermoelectric generator reaches an output power density of 0.323 μW cm⁻² at ΔT = 10 K. ### Summary This research successfully prepared PEDOT:PSS fibers with excellent thermoelectric and mechanical properties by regulating polymer chain arrangement and adopting continuous wet - spinning process, providing a new approach for the development of high - performance organic thermoelectric materials and demonstrating their application potential in the field of wearable energy harvesting.