Wood-Inspired Anisotropic Cellulose Nanofibril Composite Sponges for Multifunctional Applications
Yiming Chen,Lin Zhang,Changtong Mei,Yang Li,Gaigai Duan,Seema Agarwal,Andreas Greiner,Chunxin Ma,Shaohua Jiang
DOI: https://doi.org/10.1021/acsami.0c10645
2020-07-16
Abstract:Nanocellulose-based porous materials have been recently considered as ideal candidates in various applications. However, challenges on performances remain owing to the disorderly structure and the limited transport specificity. Herein, wood-inspired composite sponges consisting of cellulose nanofibrils (CNFs) and high-aspect-ratio silver nanowires (AgNWs) were generated with anisotropic properties by the directional freeze-drying. The obtained composite sponges exhibited attractive features, such as an excellent compressive stress of 24.5 kPa, low percolation threshold of 0.1 vol % AgNWs, and high electrical conductivity of 1.52 S/cm. Furthermore, the self-assembled ordered structure in the longitudinal direction and synergistic effect between CNFs and AgNWs benefited the sponge interesting anisotropic electrical conductivity, thermal diffusivity, ultrafast electrically induced heating (<5 s), sensitive pressure sensing (errors <0.26%), and electromagnetic interference (EMI) shielding for special practical demands. This multifunctional material inspired by natural woods is expected to broaden new applications as electronic devices for an intelligent switch or EMI shielding.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c10645?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c10645</a>.Characterizations of raw materials (Figure S1); the stability of the precursor dispersions (Figure S2); SEM images of conductive CA-d sponges with 0.4 and 0.5 vol % AgNWs (Figure S3); SEM images of conductive CA-n sponges with different volume fractions of AgNWs (Figure S4); the pore distributions and XRD patterns of conductive sponges (Figure S5); resistance values of CA-d-longitudinal sponges with different volume fractions of AgNWs (Figure S6); the dependence of the conductivity (σ) on the volume fraction of AgNWs (Figure S7); resistance values of CA-d-transverse sponges with different volume fractions of AgNWs (Figure S8); resistance values of CA-n sponges with different volume fractions of AgNWs (Figure S9); density and porosity of CA-d (Table S1); the summary of density and EMI parameters for typical porous materials (Table S2); comparison between true and experimental values (Table S3) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c10645/suppl_file/am0c10645_si_001.pdf">PDF</a>)Simulation of EMI shielding application of the sponge of CA-d-0.3 without an iron cover, and with an iron cover, respectively (Video S1) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c10645/suppl_file/am0c10645_si_002.avi">AVI</a>)Simulation of EMI shielding application of the sponge of CA-d-0.3 with an iron cover having an unobstructed hole, and with an iron cover having a hole covered with an iron sheet, respectively (Video S2) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c10645/suppl_file/am0c10645_si_003.avi">AVI</a>)Simulation of EMI shielding application of the sponge of CA-d-0.3 with an iron cover having a hole covered with the longitudinal plane of the sponge, and with an iron cover having a hole covered with the transverse plane of the sponge, respectively (Video S3) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c10645/suppl_file/am0c10645_si_004.avi">AVI</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology