CsPb2Br5 assisted direct crystallization of 3D perovskite phase for highly efficient and stable solar cells
Caiyun Gao,Kun Gao,Bingqian Zhang,Xiuhong Sun,Qiangqiang Zhao,Xiao Wang,Feng Wang,Mingliang Sun,Guanglei Cui,Shuping Pang,KUN GAO
DOI: https://doi.org/10.1039/d4ee00229f
IF: 32.5
2024-03-27
Energy & Environmental Science
Abstract:Improving the crystallization quality of the perovskite film is crucial for both the efficiency and stability of perovskite solar cells. However, the solid-state transition of formamidinium lead iodide perovskite thin films from the δ to α phase at high temperatures typically introduces a significant number of lattice defects, which inturn leads to increased carrier recombination rates and reduced humidity stability. Directly growing the α-phase perovskite phase from the precursor solution still remains a challenge. In this work, a low solubility, halogen rich CsPb2Br5 crystal was introduced into the perovskite solution to regulate the crystallization behavior of the perovskite layer. It was demonstrated that the CsPb2Br5 nanocrystals were pre-precipitated and induced the direct crystallization of the α-phase perovskite during the solution processing. The direct formation of the α-phase instead of the δ-phase effectively enhances the crystalline quality and reduces the defect density of the perovskite films. As a result, the corresponding device exhibits an enhanced power conversion efficiency of 25.55%, and the module efficiency with 14 cm2 of active area achieves 22.35% (certified PCE was 21.7%). Thanks to the higher crystalline quality, these unencapsulated devices exhibit excellent operational stability at the maximum power point (~92% efficiency retention after 1000 h).
energy & fuels,chemistry, multidisciplinary,engineering, chemical,environmental sciences