Abstract:Copper as well as copper base composites reinforced with coated and uncoated 1 wt% diamond, graphite particles or short carbon fibers are prepared by powder metallurgy process. The reinforcement particles were encapsulated with silver as well as copper layer by using the electroless deposition technique to investigate the influence of the reinforcement surface coating on the microstructure, density, electrical and thermal properties of the sintered samples. The coated and the uncoated powders were cold compacted at 600 MPa, and then sintered at 1173 K (900°C) for 2 h under hydrogen atmosphere. The phase composition, morphology and microstructure of the prepared powders as well as the copper base sintered composites were investigated using X-ray diffraction analysis (XRD) and Scanning Electron Microscope (SEM) equipped with an Energy Dispersive Spectrometer (EDS) respectively. The density of the sintered composites was measured by Archimedes method. The copper base consolidated composites had a density up to 96% and the reinforcement coated particles were distributed uniformly within the copper matrix better than the uncoated one. The electrical resistivity at room temperature and the heat transfer conduction of the produced samples were measured in a temperature range between 323 K (50°C) and 393 K (120°C). The results observed that the sintered materials prepared from the coated powder have lower electrical resistivity than the sintered materials prepared from the mixed powders. On the other hand the thermal conductivity values were calculated using the heat transfer conduction values by means of the Fourier formula. The results observed that the thermal conductivity of copper is (391 W/m·K), 1 wt% diamond/Cu is (408 W/m·K), 1 wt% graphite coated silver/Cu is (393 W/m·K), 1 wt% Cu coated short carbon fiber/Cu is (393 W/m·K), graphite/Cu is (383 W/m·K) and short carbon fiber/Cu is (382 W/m·K). The obtained composites are expected to be suitable for heat sink applications. The heat transfer testing experiments were done. The forced convection of the present work was done and compared with the previous work in the literature, and satisfactory agreement was achieved.

Preparation of high thermal conductivity shaped diamond/copper composites by isostatic pressing

Effect of Hot-Pressing Pressure on the Microstructure and Thermal Conductivity of Copper/Ti-Coated Diamond Composites

High thermal conductivity of diamond/copper composites produced with Cu–ZrC double-layer coated diamond particles

Fabrication of diamond/copper composite thin plate based on a single-layer close packed diamond particles network for heat dissipation

Thermal Conductivity and Sintering Mechanism of Aluminum/Diamond Composites Prepared by DC-Assisted Fast Hot-Pressing Sintering

High thermal conductive copper/diamond composites: state of the art

Progress in the Copper-Based Diamond Composites for Thermal Conductivity Applications

Effect of structural modification on the thermophysical properties of graphite films/diamond sandwich copper thermally conductive composite film

Enhanced Interfacial Bonding in Copper/Diamond Composites via Deposition of Nano-copper on Diamond Particles

Effects of Diamond Content on the Thermal Conductivity of Copper Matrix Composite Materials Prepared by Cold Spraying

Highly Conductive Graphite Matrix/copper Composites by a Pressureless Infiltration Method

High thermal conductivity Cu-3Cr/Diamond composites fabricated by powder metallurgy

Microstructure and Properties of W Cu Composites with Low Copper Content at Different Sintering Temperatures

Thermal properties of tungsten/tungsten carbide-coated double-size diamond/copper composite

Microstructure and high-temperature mechanical properties of Cu-W composite prepared by hot isostatic pressing

Effects of Cold Spraying Process and Diamond Addition on Microstructure and Thermal Conductivity of Copper Matrix Composites

Preparation and thermal conductivity of tungsten coated diamond/copper composites

Fabrication of Titanium and Copper-Coated Diamond/Copper Composites via Selective Laser Melting

Fabrication, Microstructure, Thermal and Electrical Properties of Copper Heat Sink Composites

Effect of sintering temperature on microstructure and properties of nano-WC particle reinforced copper matrix composites prepared by hot-pressing sintering

Interfacial characterization and thermal conductivity of diamond/Cu composites prepared by two HPHT techniques