Abstract:This study investigates the alternative of replacing noble metals by base metals as catalysts for selective hydrogenation of polyunsaturated hydrocarbons. Nickel catalysts are active for this type of reaction, but poorly selective. However, former calculations anticipated that Ni–Zn alloys could have higher selectivity to alkenes than monometallic Ni depending on the Ni/Zn atomic ratio in the alloy. In this contribution, Ni–Zn alloy nanoparticles supported on TiO2 are synthesized as catalysts for selective hydrogenation of acetylene and butadiene. The designed catalysts with 0.5 wt% Ni loading and various Ni/Zn nominal ratios are prepared by deposition–precipitation with urea (DPU). STEM-HAADF imaging coupled with EDS analysis reveals that Ni–Zn bimetallic particles are formed after reduction treatment at 450 °C. Alloying Ni with Zn leads to a slight increase in the average particle size and a broadening of the size distribution compared to monometallic Ni. However, the average Ni/Zn atomic ratio measured by EDS in the bimetallic particles is always higher than the nominal one, which could be due to Zn evaporation under the beam. The results of acetylene hydrogenation show that although the catalytic activity is slightly reduced after alloying Ni with Zn, the selectivity to ethylene is enhanced from 50% up to 85%, at the expense of the formation of oligomers (coupling products). However, the bimetallic Ni–Zn catalysts suffer from progressive deactivation in this reaction. During butadiene hydrogenation performed in the presence of an excess of propene, the bimetallic Ni–Zn/TiO2 catalysts are significantly more stable, with a high and constant selectivity to butenes (> 95%), compared with Ni/TiO2, which deactivates rapidly in the first hours. Some hypotheses concerning the observed differences in catalytic stability are discussed.

InNi 3 C 0.5 @C-derived InNi 3 alloy as a coke-resistant low-temperature catalyst for selective butadiene hydrogenation

Engineering MOx/Ni Inverse Catalysts for Low-Temperature CO2 Activation with High Methane Yields

Promotional effects of Nb 2 O 5 on ceria doped Ni catalysts for selective hydrogenation of 1,3-butadiene to butenes: Combined experimental and DFT approach

An efficient NiCu@C/Al 2 O 3 catalyst for selective hydrogenation of acetylene

Bimetallic Ni–Zn/TiO2 catalysts for selective hydrogenation of alkyne and alkadiene impurities from alkenes stream

Unveiling the Origin of Enhanced Catalytic Performance of NiCu Alloy for Semi-Hydrogenation of Acetylene

Theoretical study the influence of partial substitute noble metal Pd/Ag of PdAg-based catalyst by non-noble metal Ni/Cu for 1,3-Butadiene hydrogenation

Subsurface carbon modification of Ni-Ga for improved selectivity in acetylene hydrogenation reaction

Understanding the Role of Coordinatively Unsaturated Al 3+ Sites on Nanoshaped Al 2 O 3 for Creating Uniform Ni–Cu Alloys for Selective Hydrogenation of Acetylene

Study on the calcination conditions of the Ni/Al2O3 catalyst to remove butadiene in fcc c4 fraction

Oxidative Dehydrogenation and Dry Reforming of N-Butane with CO2 over NiFe Bimetallic Catalysts

Cobalt-doped Ni-based catalysts for low-temperature CO 2 methanation

Significant effect of In doping on Ni/C catalyst for hydrogenation of dimethyl oxalate to ethanol: Synergistic effect of InNi 3 alloy, surface oxygen, and defect sites

CO2 Methanation over CoNi Bimetal-Doped Ordered Mesoporous Al2O3 Catalysts with Enhanced Low-Temperature Activities

InNi3C0.5/Fe3O4 catalyst for the CO2 hydrogenation to methanol: Co-precipitation preparation, performance and mechanistic insight

Selective hydroisomerization of isobutane to n-butane over WO3-ZrO2 supported Ni-Cu alloy

Nickel Carbide (Ni3C) Nanoparticles for Catalytic Hydrogenation of Model Compounds in Solvent

Revealing the effect of metal-support interactions at the Ni/In2O3(111) interface on the selective CO2 hydrogenation

Iron-nickel alloy particles with N-doped carbon "armor" as a highly selective and long-lasting catalyst for the synthesis of N-benzylaniline molecules

Effect of Carbon Modification on the Performance of NiO/gamma-Al2O3 Catalyst for Isobutane Dehydrogenation

Novel preparation method of bimetallic Ni-In alloy catalysts supported on amorphous alumina for the highly selective hydrogenation of furfural