Toward Reducing Casting Defects via 3D Risers via 3D Sand-Printing: A Simulation Study

Manogharan, Guha

DOI: https://doi.org/10.1007/s40962-024-01353-1

2024-05-16

International Journal of Metalcasting

Abstract:The 3D sand printing (3DSP) process is a binder jetting class of additive manufacturing process that can incorporate complex 3D mold designs and consolidate cores with intricate features that were previously inaccessible. Prior studies in 3DSP mold design have been shown to improve pouring and filling conditions for sand casting. However, the opportunity to improve casting quality by exploring 3D riser designs during the solidification stage has not yet been explored. In this research, three novel 3D riser geometries—ellipsoid, spherical, and a fusion riser (combination of cylindrical and ellipsoid riser) were investigated. The results were compared to the benchmark cylindrical risers to assess casting performance (e.g., reduction in shrinkage porosity, increase in solidification time). Computational solidification simulations have been presented to evaluate the characteristics of the novel risers for three different metal alloys- nickel aluminum bronze (NAB), low-carbon steel A216 (WCB), and aluminum alloy (A319) alloy. From the results of this research, spherical risers were found to provide 45% yield improvement of for the three alloys studied. In addition, the riser neck diameter using a spherical riser experienced up to 77% reduction when compared to the recommended dimensions from previous literature. Finally, one of the spherical riser designs provided 18% improvement in terms of riser-pipe safety height over the benchmark design. Findings from this research will help metalcasting industries to optimize their riser designs for complex casting geometries by implementing 3D riser geometries (via 3DSP) into traditional mold making for yield improvement and defect-free castings.

metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The paper aims to address the issue of shrinkage defects in the casting process. Specifically, the research explores new three-dimensional riser designs under the three-dimensional sand printing (3DSP) technology to reduce casting defects and improve casting performance. The following is an overview of the problems the paper attempts to solve:

1. **Limitations of Traditional Riser Design**:
- In traditional casting, only cylindrical risers are used. Their design is limited by mold manufacturing processes, resulting in larger riser volumes that affect casting yield.

2. **Study of New Riser Geometries**:
- Explore three new three-dimensional riser designs (ellipsoidal, spherical, and hybrid risers) and compare them with traditional cylindrical risers to evaluate the effectiveness of different riser designs in reducing shrinkage defects.

3. **Simulation Study**:
- Use computational solidification simulation to evaluate the performance of new risers in different metal alloys (nickel-aluminum bronze, low alloy steel, aluminum alloy), focusing mainly on shrinkage reduction and extended solidification time.

4. **Optimization of Riser Design**:
- Simulation studies reveal that spherical risers can significantly improve casting performance and reduce the riser neck diameter, thereby increasing casting yield and quality.

5. **Practical Application Prospects**:
- The research findings are expected to help the metal casting industry optimize riser design through the implementation of 3D sand printing technology, achieving defect-free production of complex castings.

In summary, the main goal of the paper is to improve casting quality and efficiency and reduce casting defects by improving riser design based on 3D sand printing technology.