Efficient degradation of perfluorooctanoic acid by electrospun lignin-based bimetallic MOFs nanofibers composite membranes with peroxymonosulfate under solar light irradiation

Chen Hou,Wenqiang Chen,Linhui Fu,Sufeng Zhang,Chen Liang,Yang Wang

DOI: https://doi.org/10.1016/j.ijbiomac.2021.01.184

IF: 8.2

2021-03-01

International Journal of Biological Macromolecules

Abstract:<p>Perfluorooctanoic acid (PFOA) has demonstrated potential toxicity to human health and has been detected in different environmental matrices due to its stable physical and chemical properties. To degrade PFOA under solar light irradiation, we fabricated a lignin/polyvinyl alcohol (PVA)/Co/Fe metal-organic frameworks (lignin/PVA/bi-MOFs) composite membrane via a typical electrospinning and in-situ solvothermal method for the catalytic degradation of PFOA. In the peroxymonosulfate (PMS)/membranes/solar light system, Electron paramagnetic resonance analysis (EPR) demonstrated the sulfate radicals (SO₄⁻) and hydroxyl radicals (OH) were generated by activating PMS with transition metal and solar light irradiation. Lignin/PVA/bi-MOFs showed outstanding performance in that 89.6% of PFOA was degraded within 3 h under optimal conditions. Compared with that in solar light, only 59.6% PFOA was degraded in the dark, and the rate constant of PFOA degradation decreased from 0.0150 min⁻¹ to 0.0046 min⁻¹. Moreover, lignin/PVA/bi-MOFs were reused after simply rinsing with ultra-pure water and the degradation capacity of lignin/PVA/bi-MOFs remained at 77% after 4 cycles. The results might provide a new concept for the design of bimetallic MOFs for applications in organic pollutant removal.</p>

polymer science,biochemistry & molecular biology,chemistry, applied

What problem does this paper attempt to address?

The paper aims to address the degradation of perfluorooctanoic acid (PFOA) in the environment. PFOA is difficult to biodegrade due to its stable physicochemical properties and has been detected in various environmental media, posing potential toxicity to human health. To effectively degrade PFOA under sunlight irradiation, researchers prepared a composite membrane composed of lignin/polyvinyl alcohol (PVA)/cobalt/iron metal-organic frameworks (lignin/PVA/bi-MOFs) through typical electrospinning and in-situ solvothermal methods.

In the system of peroxymonosulfate (PMS), composite membrane, and sunlight irradiation, electron paramagnetic resonance (EPR) analysis indicated that transition metals and sunlight irradiation activated PMS to generate sulfate radicals (SO4•−) and hydroxyl radicals (OH•). Experimental results showed that under optimal conditions, 89.6% of PFOA was degraded within 3 hours. Compared to a 59.6% degradation rate under sunlight irradiation alone, the degradation efficiency of this composite membrane was significantly improved under dark conditions. Additionally, after a simple ultrapure water rinse, the lignin/PVA/bi-MOFs composite membrane maintained 77% degradation capability after 4 cycles. These results provide new concepts for designing bimetallic MOFs for the removal of organic pollutants.