Effects of Magnesium Mineral on the Reduction and Expansion Performances of Baiyun Ebo Iron Pellets

Yongbin Wang,Jun Peng,Shuang Liu,Guoping Luo,Fang Zhang,Shengli An
DOI: https://doi.org/10.3390/met14010116
IF: 2.695
2024-01-18
Metals
Abstract:Pellet ore is an important raw material for blast furnace ironmaking, and its reduction and expansion performance directly affects the smooth operation and smelting indicators of the blast furnace. This paper quantitatively studied the effects of magnesium minerals such as dolomite and serpentinite on the pellet-forming performance, the microstructure after roasting, compressive strength, and the reduction expansion performance of Baiyun Ebo iron concentrate. The optimal ratio of dolomite and serpentinite to add was determined when preparing pellets using Baiyun Ebo iron concentrate powder. The results showed that the drop strength and compressive strength of the green pellet after adding serpentine were relatively higher than those after adding dolomite, indicating that controlling the MgO content in the green pellet at 2.5% using serpentine was beneficial for improving the drop strength and compressive strength. Under the condition of adding dolomite, when the MgO content was 2.5%, the compressive strength of the roasted pellet was the highest, which was 2192.6 N, and the volume expansion rate was 12.32%. Under the condition of adding serpentine, when the MgO content was 2.5%, the compressive strength of the roasted pellet was 2622.2 N, and the volume expansion rate was 9.71%. Compared with dolomite as a magnesium additive, when the reduction expansion rate of Baiyun Ebo iron concentrate was controlled within 20%, serpentine only needed to have a MgO content of about 1.5% in the pellets, while dolomite needed to have a MgO content of about 2.5%. Therefore, under the condition that the MgO contents of dolomite and serpentine were equivalent, the amount of serpentine used was lower.
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The paper aims to study the reduction swelling properties of Bayan Obo iron ore concentrate pellets after adding different proportions of dolomite and serpentine, and their impact on pellet performance. ### Problems the paper attempts to solve: 1. **Reduction Swelling Properties**: Investigate the reduction swelling behavior of Bayan Obo iron ore concentrate pellets after adding dolomite and serpentine to improve their application in the blast furnace ironmaking process. 2. **Pellet Performance Optimization**: Determine the optimal proportion of dolomite and serpentine to add during the preparation of Bayan Obo iron ore concentrate pellets to enhance the drop strength and compressive strength of the pellets. 3. **Microstructure Changes**: Through quantitative analysis of the effects of different proportions of dolomite and serpentine on pellet formation performance, post-sintering mineral phase structure, compressive strength, and reduction swelling properties, find the optimal addition ratio. ### Main Findings: - After adding serpentine, the drop strength and compressive strength of the pellets are higher than when adding dolomite, especially when the MgO content is 2.5%, achieving the best effect. - In the case of adding dolomite, when the MgO content is 2.5%, the compressive strength of the sintered pellets is the highest at 2192.6 N, with a volume expansion rate of 12.32%. - In the case of adding serpentine, when the MgO content is 2.5%, the compressive strength of the sintered pellets is 2622.2 N, with a volume expansion rate of 9.71%. - Compared to dolomite, adding serpentine can significantly reduce the reduction swelling rate of the pellets, and the amount of serpentine added is lower to achieve the same MgO content.